Effects of Sr on the microstructure and electrical properties of (Co, Ta)-doped SnO2 varistors

被引：0

作者：

Wang, Jin-Feng ^{[1
]}

Chen, Hong-Cun ^{[1
]}

Su, Wen-Bin ^{[1
]}

Zang, Guo-Zhong ^{[1
]}

Wang, Biao ^{[1
]}

Gao, Ru-Wei ^{[1
]}

机构：

[1] School of Physics and Microelectronics, State Key Laboratory of Crystal Materials, Shandong University, Jinan 250100, China

来源：

Journal of Alloys and Compounds | 2006年 / 413卷 / 1-2期

关键词：

The effect on the microstructure and electrical properties of (Co; Ta)-doped SnO2 varistors upon the addition of SrCO3 was investigated. The threshold electric field of the SnO2-based varistors increased significantly from 318 to 3624 V/mm; the relative dielectric constants of the SnO2-based varistors decreased greatly from 1509 to 69 as SrCO3 concentration was increased up to 2.5 mol%. The significant decrease of the SnO2 grain size; from 8.19 to 1.03 μm with increasing SrCO3 concentration over the range of 0-2.5 mol%; is the origin for increase in the threshold voltage and decrease of the dielectric constants. The grain size reduction is attributed to the segregation of SrCO3 at grain boundaries hindering the SnO2 grains from conglomerating into large particles. Varistors were found to have superhigh threshold voltage and comparatively large nonlinear coefficient α. For 1.5 mol% SrCO3-doped sample; threshold electrical field E and nonlinear coefficient α were measured to be 1738 V/mm and 23.7; for 2.0 mol% SrCO3-doped sample; E and α were 2204 V/mm and 24; and for 2.5 mol% SrCO3-doped sample; E and α were 3624 V/mm and 22. Superhigh threshold voltage and large nonlinear coefficient qualify the Sr-doped SnO2 varistor as an excellent candidate in use for high voltage protection system. The reasons why the grain resistivity of the SnO 2-based varistors increased with increasing SrCO3 concentration and the boundary resistivity of the SnO2-based varistors gradually decreased with increasing SrCO3 concentration were explained. © 2005 Elsevier B.V. All rights reserved;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Journal article (JA)

引用

页码：35 / 39

共 50 条

[11] Effect of high Al2O3 content on the microstructure and electrical properties of Co- and Ta-doped SnO2 varistors
Chiquito, M. P. Torres
Pech-Canul, M. I.
Hernandez, M. B.
Garcia-Quinonez, L. V.
Davila, M. Montoya
Aguilar-Martinez, J. A.
JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS, 2019, 30 (18) : 17342 - 17349
[12] Electrical properties of SnO2 varistors
Castro, MS
Aldao, CM
ANALES DE LA ASOCIACION QUIMICA ARGENTINA, 1995, 83 (06): : 379 - 382
[13] Effects of Sc2O3 on the microstructure and varistor properties of (Co, Ta)-doped SnO2
Zang, GZ
Wang, JF
Chen, HC
Su, WB
Wang, WX
Wang, CM
Qi, P
JOURNAL OF ALLOYS AND COMPOUNDS, 2004, 377 (1-2) : 82 - 84
[14] Effect of CaO on the microstructure and non-ohmic properties of (Co,Sb)-doped SnO2 varistors
Aguilar-Martinez, J. A.
Duran-Regules, A.
Glot, A. B.
Hernandez, M. B.
Pech-Canul, M. I.
Castillo-Torres, J.
REVISTA MEXICANA DE FISICA, 2008, 54 (01) : 20 - 24
[15] Effect of Gd2O3 on the electrical properties of (Co, nb)-doped SnO2 varistors
Zang, GZ
Wang, JF
Chen, HC
Su, WB
Wang, CM
Qi, P
Ming, BQ
HIGH-PERFORMANCE CERAMICS III, PTS 1 AND 2, 2005, 280-283 : 271 - 274
[16] Effects of Cr2O3 on the properties of (Co, Nb)-doped SnO2 varistors
Wang, WX
Wang, JF
Chen, HC
Su, WB
Zang, GZ
MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY, 2003, 99 (1-3): : 470 - 474
[17] Influence of Ta2O5 on the electrical properties of ZnO- and CoO-doped SnO2 varistors
Filho, FM
Simoes, AZ
Ries, A
Silva, IP
Perazolli, L
Longo, E
Varela, JA
CERAMICS INTERNATIONAL, 2004, 30 (08) : 2277 - 2281
[18] Electrical conduction in SnO2 varistors
Glot, A. B.
Gaponov, A. V.
Sandoval-Garcia, A. P.
PHYSICA B-CONDENSED MATTER, 2010, 405 (02) : 705 - 711
[19] Varistors Based on Doped SnO2
Sanjay R. Dhage
Violet Samuel
V. Ravi
Journal of Electroceramics, 2003, 11 : 81 - 87
[20] Varistors based on doped SnO2
Dhage, SR
Samuel, V
Ravi, V
JOURNAL OF ELECTROCERAMICS, 2003, 11 (1-2) : 81 - 87

← 1 2 3 4 5 →