Failure mechanisms of a PCD tool in high-speed face milling of Ti-6Al-4V alloy

被引：0

作者：

机构：

[1] Li, Anhai

[2] Zhao, Jun

[3] Wang, Dong

[4] Zhao, Jiabang

[5] Dong, Yongwang

来源：

Zhao, J. (zhaojun@sdu.edu.cn) | 1959年 / Springer London卷 / 67期

关键词：

High-speed milling tests were carried out on Ti-6Al-4V titanium alloy with a polycrystalline diamond (PCD) tool. Tool wear morphologies were observed and examined with a digital microscope. The main tool failure mechanisms were discussed and analyzed utilizing scanning electron microscope, and the element distribution of the failed tool surface was detected using energy dispersive spectroscopy. Results showed that tool flank wear rate increased with the increase in cutting speed. The PCD tool is suitable for machining of Ti-6Al-4V titanium alloy with a cutting speed around 250 m/min. The PCD tool exhibited relatively serious chipping and spalling at cutting speed higher than 375 m/min, within further increasing of the cutting speed the flank wear and breakage increased greatly as a result of the enhanced thermal-mechanical impacts. In addition, the PCD tool could hardly work at cutting speed of 1,000 m/min due to the catastrophic fracture of the cutting edge and intense flank wear. There was evidence of workpiece material adhesion on the tool rake face and flank face in very close proximity to the cutting edge rather than on the chipped or flaked surface, which thereby leads to the accelerating flank wear. The failure mechanisms of PCD tool in high-speed wet milling of Ti-6Al-4V titanium alloy were mainly premature breakage and synergistic interaction among adhesive wear and abrasive wear. © Springer-Verlag London 2012;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Journal article (JA)

引用

页码：9 / 12

共 50 条

[21] Experimental study and modeling of cutting force in high-speed milling of Ti-6Al-4V titanium alloy
Mou, Huahong
Xue, Wenchao
Wu, Lan
Zhang, Ziyuan
Tu, Zhibiao
Lian, Zhibiao
JOURNAL OF MECHANICS, 2025, 41 : 55 - 63
[22] Experimental investigation on chip morphologies in high-speed dry milling of titanium alloy Ti-6Al-4V
Anhai Li
Jun Zhao
Yonghui Zhou
Xiaoxiao Chen
Dong Wang
The International Journal of Advanced Manufacturing Technology, 2012, 62 : 933 - 942
[23] Experimental investigation on chip morphologies in high-speed dry milling of titanium alloy Ti-6Al-4V
Li, Anhai
Zhao, Jun
Zhou, Yonghui
Chen, Xiaoxiao
Wang, Dong
INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2012, 62 (9-12): : 933 - 942
[24] Surface integrity characterization in high-speed dry end milling of Ti-6Al-4V titanium alloy
H. Safari
S. Sharif
S. Izman
H. Jafari
The International Journal of Advanced Manufacturing Technology, 2015, 78 : 651 - 657
[25] Microstructure attributes and tool wear mechanisms during high-speed machining of Ti-6Al-4V
Sharma, Shiv
Meena, Anil
JOURNAL OF MANUFACTURING PROCESSES, 2020, 50 : 345 - 365
[26] Investigations on the machining characteristics of Ti-6Al-4V alloy during high-speed end milling process
Samsudeensadham, S.
Krishnaraj, V.
Thilak, R. Keshav
Prasath, V.
INTERNATIONAL JOURNAL OF MANUFACTURING RESEARCH, 2023, 18 (02) : 125 - 143
[27] Surface integrity characterization in high-speed dry end milling of Ti-6Al-4V titanium alloy
Safari, H.
Sharif, S.
Izman, S.
Jafari, H.
INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2015, 78 (1-4): : 651 - 657
[28] Numerical investigation on serrated chip formation during high-speed milling of Ti-6Al-4V alloy
Ullah, Irfan
Zhang, Song
Zhang, Qing
Wang, Renwei
JOURNAL OF MANUFACTURING PROCESSES, 2021, 71 : 589 - 603
[29] Experimental study on the chip morpholgy in high speed milling Ti-6Al-4V alloy
School of Mechanical and Power Engineering, North University of China, Taiyuan
030051, China
不详
030024, China
Jixie Gongcheng Xuebao, 3 (196-205):
[30] Surface integrity in high speed end milling of titanium alloy Ti-6Al-4V
Daymi, A.
Boujelbene, M.
Ben Amara, A.
Bayraktar, E.
Katundi, D.
MATERIALS SCIENCE AND TECHNOLOGY, 2011, 27 (01) : 387 - 394

← 1 2 3 4 5 →