Microstructure and properties of borosilicate glass coating for oxidation protection of C/SiC brake materials

被引：0
|
作者：
Yao, Ning-Na [1 ]
Cheng, Lai-Fei [1 ]
Xu, Yong-Dong [1 ]
Zhang, Li-Tong [1 ]
Fan, Shang-Wu [1 ]
机构：
[1] National Key Laboratory of Thermostructure Composites Materials, Northwestern Polytechnical University, Xi'an 710072, China
来源：
Guti Huojian Jishu/Journal of Solid Rocket Technology | 2007年 / 30卷 / 04期
关键词：
Coatings - Corrosion resistance - Oxidation resistance - Sol-gels - Substrates - Temperature - Thermal shock;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The borosilicate glass coating for oxidation protection of C/SiC brake materials was prepared by sol-gel method. The formation process from sol to glass was investigated by FTIR, XRD and TG-DSC, and the capabilities of oxidation resistance and thermal shock resistance were analyzed. The results show that the borosilicate glass coating was uniform and dense, moreover it can be closely boned with the composite substrates. At 800°C, the borosilicate glass coating has excellent capabilities of oxidation resistance and thermal shock resistance, high-temperature stability as well as superior sea water corrosion resistance. After the coating samples were oxidized for 10h at 800°C, weight loss ratio of the samples with and without sea water immersion was about 2.36% and 0.33% respectively, After thermal shock for 50 times (10h), the coating remained undamaged, and the weight loss was about 9.79%.
引用
收藏
页码：358 / 361
相关论文
共 50 条
  • [41] CNT-PyC-SiC/SiC double-layer oxidation-protection coating on C/C composite
    Zheng, Guo-Bin
    Mizuki, Hironori
    Sano, Hideaki
    Uchiyama, Yasuo
    CARBON, 2008, 46 (13) : 1808 - 1811
  • [42] Preparation and oxidation resistance of mullite/SiC coating for carbon materials at 1150 °C
    Yang Xin
    Su Zhe-an
    Huang Qi-zhong
    Chai Li-yuan
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2012, 22 (12) : 2997 - 3002
  • [43] Effect of thermal exposure on microstructure of borosilicate glass coating on ceramic insulation tile
    Sun, Yu-Lei
    Li, Ming-Wei
    Zhong, Ye-Sheng
    Shi, Li-Ping
    He, Xiao-Dong
    Surface Technology, 2019, 48 (01): : 83 - 89
  • [44] Microstructure and mechanical properties of low-activation glass-ceramic joining and coating for SiC/SiC composites
    Katoh, Y
    Kotani, M
    Kohyama, A
    Montorsi, M
    Salvo, M
    Ferraris, M
    JOURNAL OF NUCLEAR MATERIALS, 2000, 283 : 1262 - 1266
  • [45] Oxidation protection of graphite and B4C-modified graphite by a SiC coating
    Guo, QG
    Song, JR
    Liu, L
    Zhang, BJ
    CARBON, 1999, 37 (01) : 149 - 152
  • [46] Oxidation protection of graphite and B4C-modified graphite by a SiC coating
    Chinese Acad of Sciences, Shanxi, China
    Carbon, 1 (149-152):
  • [47] Microstructure and anti-oxidation properties of Yb2Si2O7/SiC bilayer coating for C/SiC composites
    Chen, Pengju
    Pan, Ling
    Xiao, Peng
    Li, Zhuan
    Pu, Dongmei
    Li, Jinwei
    Pang, Liang
    Li, Yang
    CERAMICS INTERNATIONAL, 2019, 45 (18) : 24221 - 24229
  • [48] Oxidation resistance and thermal cycling properties of the SiCnws-SiC coating on the C/SiC composites
    Wang, Bo
    Zhang, Fan
    Hao, Jianjie
    He, Ping
    Shi, Wei
    Tan, Yi
    Li, Jiayan
    INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY, 2023, 20 (03) : 1793 - 1803
  • [49] Microstructure and oxidation resistance of SiC–MoSi2 multi-phase coating for SiC coated C/C composites
    Zibo He
    Hejun Li
    Xiaohong Shi
    Qiangang Fu
    Heng Wu
    Progress in Natural Science:Materials International, 2014, 24 (03) : 247 - 252
  • [50] Microstructure and oxidation resistance of SiC-MoSi2 multi-phase coating for SiC coated C/C composites
    He, Zibo
    Li, Hejun
    Shi, Xiaohong
    Fu, Qiangang
    Wu, Heng
    PROGRESS IN NATURAL SCIENCE-MATERIALS INTERNATIONAL, 2014, 24 (03) : 247 - 252
12345