Fracture toughness of 7475-T7351 aluminum alloy thick plate

被引：1
|
作者：
Chen, Jun [1 ,2 ]
Duan, Yulu [2 ]
Peng, Xiaoyan [2 ]
Cao, Xiaowu [2 ]
Xu, Guofu [2 ,3 ]
Yin, Zhimin [2 ,3 ]
机构：
[1] Powder Metallurgy Research Institute, Central South University, Changsha,410083, China
[2] School of Materials Science and Engineering, Central South University, Changsha,410083, China
[3] Key Laboratory of Nonferrous Materials Science and Engineering of Ministry of Education, Central South University, Changsha,410083, China
来源：
Zhongnan Daxue Xuebao (Ziran Kexue Ban)/Journal of Central South University (Science and Technology) | 2015年 / 46卷 / 02期
关键词：
20;
D O I：
10.11817/j.issn.1672-7207.2015.02.009
中图分类号：
学科分类号：
摘要：
引用
收藏
页码：437 / 443
相关论文
共 50 条
  • [41] 热暴露对7475-T7351铝合金组织与性能的影响
    彭小芒
    尹志民
    陈军
    沈凯
    郭加林
    王华
    中国有色金属学报, 2008, (10) : 1781 - 1787
  • [42] Dynamic fracture behaviour of AA7475-T7351 alloy at different strain rates and temperatures
    Chakraborty, Purnashis
    Tiwari, Vikrant
    ENGINEERING FRACTURE MECHANICS, 2023, 279
  • [43] 航空用7475-T7351铝合金厚板耐腐蚀性能
    刘铭
    李惠曲
    陈军洲
    李国爱
    陈高红
    材料工程, 2017, 45 (09) : 129 - 135
  • [44] 7475-T7351合金板材不同取向条件下的组织与性能
    陈军
    段雨露
    彭小燕
    钱键
    徐国富
    尹志民
    特种铸造及有色合金, 2015, 35 (01) : 1 - 4
  • [45] Corrosion fatigue crack growth of 7475 T7351 aluminum alloy under flight simulation loading
    Chemin, A.
    Spinelli, D.
    Bose, W. Filho
    Ruchert, C.
    3RD INTERNATIONAL CONFERENCE ON MATERIAL AND COMPONENT PERFORMANCE UNDER VARIABLE AMPLITUDE LOADING, VAL 2015, 2015, 101 : 85 - 92
  • [46] High-velocity impact performance of AA 7475-T7351 aluminum square plates struck by steel projectiles: Assessing leakage limit velocity
    Ataabadi, Pouria. B.
    Assuncao, Caio Magno de
    Chakraborty, Purnashis
    Alves, Marcilio
    INTERNATIONAL JOURNAL OF IMPACT ENGINEERING, 2024, 187
  • [47] 恒幅加载下7475-T7351铝合金的疲劳裂纹扩展行为
    张诗捷
    Nowack
    H.
    航空学报, 1987, (03) : 171 - 177
  • [48] Effect of aging on fracture toughness and stress corrosion cracking resistance of forged 7475 aluminum alloy
    Li, Hongying
    Geng, Jinfeng
    Dong, Xianjuan
    Wang, Changjian
    Zheng, Feng
    JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2007, 22 (02): : 191 - 195
  • [49] Effect of Aging on Fracture Toughness and Stress Corrosion Cracking Resistance of Forged 7475 Aluminum Alloy
    李红英
    Journal of Wuhan University of Technology(Materials Science Edition), 2007, (02) : 191 - 195
  • [50] Effect of aging on fracture toughness and stress corrosion cracking resistance of forged 7475 aluminum alloy
    Hongying Li
    Jinfeng Geng
    Xianjuan Dong
    Changjian Wang
    Feng Zheng
    Journal of Wuhan University of Technology-Mater. Sci. Ed., 2007, 22 : 191 - 195
12345