The effect of nano-sized precipitates on stress corrosion cracking propagation of Alloy 718 under constant loads in PWR primary water

被引：0
|
作者：
Wang, Jiamei [1 ]
Zhu, Tianyu [1 ]
Wu, Yule [1 ]
Chen, Kai [1 ]
Guo, Xianglong [1 ]
Ren, Quanyao [2 ]
Li, Yuanming [2 ]
Tang, Chuanbao [2 ]
Yi, Hongpu [2 ]
Ye, Liang [4 ]
Xu, Shihao [4 ]
Zhang, Jing [3 ]
Tian, Wenxi [3 ]
Zhang, Lefu [1 ]
机构：
[1] Shanghai Jiao Tong Univ, Sch Nucl Sci & Engn, Shanghai 200240, Peoples R China
[2] Nucl Power Inst China, Sci & Technol Reactor Syst Design Technol Lab, Chengdu 610213, Peoples R China
[3] Xi An Jiao Tong Univ, Sch Energy & Power Engn, Xian 710049, Peoples R China
[4] China Nucl Power Technol Res Inst Co Lto, Shenzhen 518000, Peoples R China
来源：
CORROSION SCIENCE | 2025年 / 242卷
关键词：
Alloy; 718; Precipitates; Stress corrosion cracking; Crack growth rate; TEM; TKD; STAINLESS-STEEL; HYDROGEN EMBRITTLEMENT; HEAT-TREATMENT; NICKEL-ALLOYS; GROWTH RATE; TEMPERATURE; SCC; BEHAVIOR; MICROSTRUCTURE; PREDICTION;
D O I：
10.1016/j.corsci.2024.112577
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The stress corrosion cracking (SCC) propagation behavior of solution-annealed and precipitation-hardened Alloy 718 was investigated. The results show gamma '' and gamma ' precipitates are beneficial on retarding its crack growth under constant loads. Nano-sized precipitates at grain boundary (GB) tend to impede GB migration and oxidation beyond the crack tip, thereby compensating for the detrimental effect of a steeper strain gradient resulting from prominent elevated yield strength. The observed 2-40 times increase in CGR in hydrogenated water (near the Ni/ NiO boundary) primarily attributes to the preferential GB oxidation and instability of the oxides during phase transition.
引用
收藏
页数：15
相关论文
共 50 条
  • [1] Influence of δ phase precipitation on the stress corrosion cracking resistance of alloy 718 in PWR primary water
    Deleume, Julien
    Cloue, Jean-Marc
    Andrieu, Eric
    JOURNAL OF NUCLEAR MATERIALS, 2008, 382 (01) : 70 - 75
  • [2] Dielectrostriction and Intergranular Stress Corrosion Cracking of Alloy 600 in PWR Primary Water
    Devine, Thomas M.
    CORROSION, PASSIVITY, AND ENERGY: A SYMPOSIUM IN HONOR OF DIGBY D. MACDONALD, 2013, 50 (31): : 91 - 97
  • [3] A study of corrosion mechanisms and kinetics of alloy 718 in PWR primary water
    Brucelle, O
    Spilmont, JG
    Cloué, JM
    Foucault, M
    Viguier, B
    Andrieu, E
    PROCEEDINGS OF THE NINTH INTERNATIONAL SYMPOSIUM ON ENVIRONMENTAL DEGRADATION OF MATERIALS IN NUCLEAR POWER SYSTEMS-WATER REACTORS, 1999, : 197 - 202
  • [4] Stress corrosion cracking of alloy 600 and alloy 690 in hydrogen/steam and PWR primary side water
    Sui, G
    Heys, GB
    Congleton, J
    PROCEEDINGS OF THE EIGHTH INTERNATIONAL SYMPOSIUM ON ENVIRONMENTAL DEGRADATION OF MATERIALS IN NUCLEAR POWER SYSTEMS - WATER REACTORS, VOLS 1 AND 2, 1997, : 274 - 281
  • [5] Microstructural characterization on intergranular stress corrosion cracking of Alloy 600 in PWR primary water environment
    Lim, Yun Soo
    Kim, Hong Pyo
    Hwang, Seong Sik
    JOURNAL OF NUCLEAR MATERIALS, 2013, 440 (1-3) : 46 - 54
  • [6] The roles of thermal mechanical treatment and δ phase in the stress corrosion cracking of alloy 718 in primary water
    Wang, M.
    Song, M.
    Was, G. S.
    Nelson, J. L.
    CORROSION SCIENCE, 2019, 160
  • [7] STRESS CORROSION CRACKING OF NICKEL WELD METALS IN PWR PRIMARY WATER
    Xiong Ru
    Zhao Yuxiang
    Liu Guiliang
    PROCEEDINGS OF THE 21ST INTERNATIONAL CONFERENCE ON NUCLEAR ENGINEERING - 2013, VOL 1, 2014,
  • [8] Stress Corrosion Cracking of Nickel Base Alloys in PWR Primary Water
    Guerre, Catherine
    Chaumun, Elizabeth
    Crepin, Jerome
    de Curieres, Ian
    Duhamel, Cecilie
    Heripre, Eva
    Herms, Emmanuel
    Laghoutaris, Pierre
    Molins, Regine
    Sennour, Mohamed
    Vaillant, Francois
    MINOS - MATERIALS INNOVATION FOR NUCLEAR OPTIMIZED SYSTEMS, 2013, 51
  • [9] STRESS CORROSION CRACKING OF ALLOY 600 IN PWR PRIMARY WATER : INFLUENCE OF CHROMIUM, HYDROGEN AND OXYGEN DIFFUSION
    Guerre, C.
    Laghoutaris, P.
    Chene, J.
    Marchetti, L.
    Molins, R.
    Duhamel, C.
    Sennour, M.
    15TH INTERNATIONAL CONFERENCE ON ENVIRONMENTAL DEGRADATION OF MATERIALS IN NUCLEAR POWER SYSTEMS-WATER REACTORS, 2011, : 1477 - 1488
  • [10] Effect of shot peening on primary water stress corrosion cracking of Alloy 600 steam generator tubes in an operating PWR plant
    Hur, DH
    Choi, MS
    Lee, DH
    Song, MH
    Kim, SJ
    Han, JH
    NUCLEAR ENGINEERING AND DESIGN, 2004, 227 (02) : 155 - 160
12345