Sub-surface cracks of borosilicate glass loaded by single grain of abrasive

被引:0
|
作者
Dai, Zihua [1 ]
Zhu, Yongwei [1 ]
Ju, Zhilan [1 ]
Li, Jun [1 ]
Sun, Tao [2 ]
Zuo, Dunwen [1 ]
机构
[1] College of Mechanical and Electrical Engineering, Nanjing University of Aeronautics and Astronautics, Nanjing,210016, China
[2] JIANGSU SINO KRYSTALS OPTROINCS Co. Ltd., Changzhou,Jiangsu,213164, China
关键词
Cracks - Grinding (machining) - Surface defects - Abrasives - Hydrofluoric acid;
D O I
10.7521/j.issn.0454-5648.2014.09.13
中图分类号
学科分类号
摘要
The process of single diamond grit acting on the K9 (borosilicate glass) workpiece surface in the process of grinding and polishing was simulated by Vickers indentation method. The crack depth of the surface occurred in the diamond head pressing was measured by HF acid section corrosion method. The relation between the crack depth and the load, as well as the pressing depth of the pressure head were investigated. The generation and development process of cracks under different loads were also analyzed by using ANSYS/LS-DYNA. The results show that the cracks are mainly the transverse cracks in the load range of 0.098-0.490N, the cracks are mainly the longitudinal crack in the load range of 0.49-2.94N, due to the massive cracks around a few of pit, and the subsurface cracks are mainly the longitudinal cracks in the load range of 2.94-9.80N. The depth of subsurface crack layer of K9 glass under different loads is 1.4-87.2 μm, and the crack depth predicted by numerical simulation is 3.5-107.5 μm.
引用
收藏
页码:1161 / 1166
相关论文
共 50 条
  • [31] Scanning electron acoustic microscopy (SEAM): A technique for the detection of contact-induced surface & sub-surface cracks
    T. F. Page
    B. A. Shaw
    Journal of Materials Science, 2004, 39 : 6791 - 6805
  • [32] Transient response of SH waves in a layered half-space with sub-surface and interface cracks
    Yang, Ping-Shung
    Liu, Shaw-Wen
    Sung, Jen-Chun
    APPLIED MATHEMATICAL MODELLING, 2008, 32 (04) : 595 - 609
  • [33] FORMATION OF SUB-SURFACE CRACKS DURING HOT ROLLING OF AUSTENITIC GRADE STAINLESS STEEL TUBES
    BORISOV, LM
    CHEMERIN.RI
    SHAIKEVI.SA
    NAIMARK, SI
    FEDOTOV, YA
    STAL IN ENGLISH-USSR, 1967, (02): : 148 - &
  • [34] Detection of Sub-Surface Cracks Using ECT with Planar Excitation Coil, GMR and TMR Sensors
    Pasadas, Dario J.
    Ramos, Helena G.
    Ribeiro, Artur L.
    ELECTROMAGNETIC NONDESTRUCTIVE EVALUATION XXII, 2019, 44 : 26 - 31
  • [35] Determining the sub-surface damage of CdTe single crystals after lapping
    O. Šik
    L. Škvarenina
    O. Caha
    P. Moravec
    P. Škarvada
    E. Belas
    L. Grmela
    Journal of Materials Science: Materials in Electronics, 2018, 29 : 9652 - 9662
  • [36] Scanning electron acoustic microscopy (SEAM): A technique for the detection of contact-induced surface & sub-surface cracks
    Page, TF
    Shaw, BA
    JOURNAL OF MATERIALS SCIENCE, 2004, 39 (22) : 6791 - 6805
  • [37] Surface and sub-surface defects on graphite after single ion impact studied with STM
    Bolse, W
    Reimann, K
    Geyer, U
    Lieb, KP
    NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS, 1996, 118 (1-4): : 488 - 492
  • [38] Surface and sub-surface defects on graphite after single ion impact studied with STM
    Bolse, W.
    Reimann, K.
    Geyer, U.
    Lieb, K.P.
    Nuclear Instruments and Methods in Physics Research, Section B: Beam Interactions with Materials and Atoms, 1996, 118 (1-4): : 488 - 492
  • [39] Numerical simulation of single abrasive grain grinding of silicon carbide surface
    Guo, Zhiquan
    Ma, Luchao
    2024 3RD INTERNATIONAL CONFERENCE ON MATERIALS ENGINEERING AND APPLIED MECHANICS, ICMEAAE 2024, 2024, 2808
  • [40] The Influence of Vibro-Assisted Abrasive Processing on the Surface Roughness and Sub-Surface Microstructure of Inconel 939 Specimen Made by LPBF
    Radziejewska, Joanna
    Marczak, Michal
    Maj, Piotr
    Glowacki, Dominik
    MATERIALS, 2023, 16 (23)