Coupling analysis of welding residual stress redistribution and crack propagation

被引：0

作者：

Gao, Hai-Yang ^{[1
]}

Luo, Guang-En ^{[1
]}

Zheng, Xin-Zhao ^{[1
]}

Chai, Ying ^{[1
]}

机构：

[1] School of Naval Architecture and Ocean Engineering, Jiangsu University of Science and Technology, Zhenjiang,212100, China

来源：

Chuan Bo Li Xue/Journal of Ship Mechanics | 2024年 / 28卷 / 11期

关键词：

Titanium alloys;

D O I：

10.3969/j.issn.1007-7294.2024.11.012

中图分类号：

学科分类号：

摘要：

Welding residual stress has a significant impact on the fatigue life of a welding structure. Meanwhile, welding residual stress is not invariable, but will be redistributed with crack propagation. Therefore, the coupling study of welding residual stress redistribution and crack propagation is very important to predict the fatigue life of a welded structure accurately. Based on thermal elastic-plastic finite element method and extended finite element method (XFEM), a fatigue life analysis method considering the coupling of residual stress redistribution and crack propagation was proposed in this paper. Taking the tensile fatigue sample of TC4 titanium alloy as an example, the redistribution of the welding residual stress along with crack propagation was studied with the extended finite element method. The welding residual stress distribution in front of the crack tip during crack propagation and the fatigue crack propagation a-N curve under the redistribution of weld residual stress were calculated by cyclic iteration. The calculation results show that the welding residual stress at the crack tip increases firstly and then decreases with the crack propagation. Compared with the results based on constant value of the residual stress, the extended finite element fatigue life analysis method considering the redistribution of the residual stress is more accurate to predict the fatigue lives of welding structures. © 2024 China Ship Scientific Research Center. All rights reserved.

引用

页码：1756 / 1767

共 50 条

[31] Prediction of the crack opening behaviour for the fatigue crack propagating in welding residual stress field
Park, EJ
Kim, EJ
Yoo, SF
ADVANCES IN NONDESTRUCTIVE EVALUATION, PT 1-3, 2004, 270-273 : 96 - 101
[32] RESIDUAL STRESS ANALYSIS BY MUTIPLE SEQUENTIAL COUPLING FOR NON-SCALLOP WELDING JOINT
Zhang, Lei
Li, Jun
Gu, Zhengjun
Zhang, Ye
ADVANCES IN STRUCTURAL ENGINEERING, PTS 1-3, 2011, 94-96 : 1334 - +
[33] Experimental investigation of fatigue crack propagation in residual stress fields
Hensel, Jonas
Nitschke-Pagel, Thomas
Rebelo-Kornmeier, Joana
Dilger, Klaus
FATIGUE DESIGN 2015, INTERNATIONAL CONFERENCE PROCEEDINGS, 6TH EDITION, 2015, 133 : 244 - 254
[34] Welding residual stresses as needed for the prediction of fatigue crack propagation and fatigue strength
Hensel, J.
Nitschke-Pagel, T.
Ngoula, D. Tchoffo
Beier, H. -Th.
Tchuindjang, D.
Zerbst, U.
ENGINEERING FRACTURE MECHANICS, 2018, 198 : 123 - 141
[35] A new approach for the influence of residual stress on fatigue crack propagation
Zhu, Lin
Jia, Min-Ping
RESULTS IN PHYSICS, 2017, 7 : 2204 - 2212
[36] Fatigue crack propagation in residual stress fields of welded plates
Galatolo, R
Lanciotti, A
INTERNATIONAL JOURNAL OF FATIGUE, 1997, 19 (01) : 43 - 49
[37] Fatigue surface crack propagation and intersecting cracks in connection with welding residual stresses
Chernyatin, A. S.
Matvienko, Yu. G.
Razumovsky, I. A.
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2018, 41 (10) : 2140 - 2152
[38] The effect of residual stress on crack propagation in a YBCO/Ag composite
Maeda, J
Nakamura, Y
Izumi, T
Shiohara, Y
SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 1999, 12 (08): : 563 - 565
[39] Effect of residual stress on crack propagation in a YBCO/Ag composite
Super. Conduct. Research Laboratory, 1-10-13 Shinonome, Koto-ku, Tokyo, 135-0062, Japan
Supercond Sci Technol, 8 (563-565):
[40] Redistribution of welding residual stress following high plastic deformation in seamless pipes
Mirzaee-Sisan, A.
Bastola, A.
INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 2017, 158 : 37 - 50

← 1 2 3 4 5 →