Influence of high temperature and pressure ammonia solution treatment on interfacial behavior of carbon fiber/epoxy resin composites

被引：0
|
作者：
Meng, L.H. [1 ]
Chen, Z.W. [1 ]
Song, X.L. [1 ]
Liang, Y.X. [1 ]
Huang, Y.D. [1 ]
Jiang, Z.X. [1 ]
机构：
[1] Department of Polymer Materials and Engineering, School of Chemical Engineering and Technology, Harbin Institute of Technology, Harbin 150001, China
来源：
Journal of Applied Polymer Science | 2009年 / 113卷 / 06期
关键词：
The method of high temperature and pressure ammonia solution treatment to improve the interfacial performances of carbon fiber/epoxy composites is discussed in this study. Besides; the influence of high temperature and pressure ammonia solution treatment on carbon fiber and its reinforced epoxy composite interface performance were studied. The untreated and treated carbon fibers were characterized by monofilament tensile test; X-ray photoelectron spectroscopy (XPS); and atomic force microscope (AFM). The interfacial adhesion of the untreated and treated carbon fibers reinforced epoxy resin composites were also evaluated by interface shear strength (IFSS) test; interlaminar shear strength (ILSS) test; and fracture morphology analysis. It was found that the interfacial adhesion of composites increased greatly after high temperature and pressure ammonia solution treatment. The improvement of interfacial adhesion was attributed to the increase of polar functional groups and surface roughness of carbon fibers surface after treatment. © 2009 Wiley Periodicals; Inc;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Journal article (JA)
引用
收藏
页码：3436 / 3441
相关论文
共 50 条
  • [21] Effect of carbon fiber surface functionality on the moisture absorption behavior of carbon fiber/epoxy resin composites
    Qian, X.
    Zhang, Y. G.
    Wang, X. F.
    Heng, Y. J.
    Zhi, J. H.
    SURFACE AND INTERFACE ANALYSIS, 2016, 48 (12) : 1271 - 1277
  • [22] Effect of Coir Fiber Surface Treatment on Interfacial Properties of Reinforced Epoxy Resin Composites
    Ru, Shaofeng
    Zhao, Can
    Yang, Songmei
    Liang, Dong
    POLYMERS, 2022, 14 (17)
  • [23] Laser Irradiation Behavior of Carbon Fiber Epoxy Resin Composites with Laminar Structure
    Yang, Yu
    Tian, Xinchun
    Ma, Zhuang
    Liu, Hanyang
    Gao, Hong
    Tian, Weizhi
    Liu, Xiaoyu
    Zhou, Zhigang
    Rogachev, Alexandr. A.
    Gao, Lihong
    CRYSTALS, 2022, 12 (12)
  • [24] Directly coating silanized nanocrystalline cellulose on carbon fiber for enhancing the interfacial adhesion of carbon fiber/epoxy resin composites
    Zhang, Mengjie
    Li, Ming
    Liu, Liu
    Fu, Junsong
    Jin, Lin
    Shang, Lei
    Xiao, Linghan
    Ao, Yuhui
    POLYMER COMPOSITES, 2019, 40 : E744 - E752
  • [25] Influence of Epoxy Resin Curing Kinetics on the Mechanical Properties of Carbon Fiber Composites
    Cruz-Cruz, Isidro
    Ramirez-Herrera, Claudia A.
    Martinez-Romero, Oscar
    Armando Castillo-Marquez, Santos
    Jimenez-Cedeno, Isaac H.
    Olvera-Trejo, Daniel
    Elias-Zuniga, Alex
    POLYMERS, 2022, 14 (06)
  • [26] Effect of high temperature immersion on properties of T800 carbon fiber/epoxy resin composites
    Xu L.
    Bian Y.-B.
    Zhou S.
    Xiao J.-H.
    Jilin Daxue Xuebao (Gongxueban)/Journal of Jilin University (Engineering and Technology Edition), 2023, 53 (07): : 1943 - 1950
  • [27] Influence of KOH solution on the tensile strength and chemical stability of carbon fiber-reinforced epoxy resin composites
    Wazzan, AA
    Al-Turaif, HA
    Daous, MA
    JOURNAL OF APPLIED POLYMER SCIENCE, 2005, 96 (05) : 1682 - 1690
  • [28] Influence of the Second-Phase Resin Structure on the Interfacial Shear Strength of Carbon Fiber/Epoxy Resin
    Liu, Hansong
    Sun, Jinsong
    Zhang, Lianwang
    Liu, Zhaobo
    Huang, Chengyu
    Sun, Mingchen
    Duan, Ziqi
    Wang, Wenge
    Zhong, Xiangyu
    Bao, Jianwen
    MATERIALS, 2024, 17 (06)
  • [29] Influence of processing temperature on interfacial behavior of HKT800 carbon fiber with BMI and epoxy matrices
    20152300908893
    Gu, Yizhuo (benniegu@buaa.edu.cn), 1600, Chinese Journal of Aeronautics (28):
  • [30] Influence of processing temperature on interfacial behavior of HKT800 carbon fiber with BMI and epoxy matrices
    Gao Aijun
    Gu Yizhuo
    Wu Qing
    Yuan Chao
    Li Min
    Zhang Zuoguang
    Chinese Journal of Aeronautics, 2015, 28 (04) : 1255 - 1262
12345