A comparison of high temperature corrosion behaviour between uncoated, Ni-Cr-Mo and Ni-Cr-Al-Y coated 316 stainless steel in ZnCl2-KCl environment

被引：0
|
作者：
Mangaladevi, Pooja [1 ]
Vijeesh, V. [2 ]
Ravishankar, K. S. [3 ]
Madav, Vasudeva [1 ]
机构：
[1] Natl Inst Technol Karnataka, Dept Mech Engn, Mangalore 575025, India
[2] Nitte Deemed Univ, NMAM Inst Technol NMAMIT, Dept Mech Engn, Nitte 574110, India
[3] Natl Inst Technol Karnataka, Dept Met & Mat Engn, Mangalore 575025, India
来源：
RESULTS IN ENGINEERING | 2025年 / 25卷
关键词：
High-temperature corrosion; Stainless steel; Degradation; Molten salt; Coatings; corrosion rate; OXIDATION; COATINGS; PROTECTION; ALLOYS;
D O I：
10.1016/j.rineng.2025.103920
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
High-temperature corrosion poses a significant challenge to the longevity and performance of materials in extreme environments. This study investigates the corrosion behavior of coated and uncoated 316 stainless steel (SS) in ZnCl2-KCl eutectic molten salt vapor at 600 degrees C. Contrary to expectations, the results indicate that uncoated 316 SS exhibits lesser corrosion compared to certain coated samples over prolonged exposure. Comprehensive analysis, including weight change measurements, electrochemical evaluations, and surface morphology examination, reveals the degradation mechanisms and the efficacy of coatings. Amongst the various materials used for study, NiCrMo coated 316SS showed least corrosion rate of 8.34 mpy and 3.2 mpy after 20 hand 100 h respectively. The findings provide insights into optimizing material protection strategies in harsh chloride containing molten salt environments.
引用
收藏
页数：8
相关论文
共 33 条
  • [31] High-Temperature Corrosion Characteristics of Ni-20Cr-xSi Alloy Laser Cladding Layer in NaCl-KCl-Na2SO4-K2SO4 Mixed Salt Environment
    Chen, Shanshan
    Liu, Zongde
    Liu, Fulai
    COATINGS, 2023, 13 (08)
  • [32] DEVELOPMENT OF MATERIAL FOR HIGH TEMPERATURE HIGH PRESSURE STEAM-TURBINE CASING .2. EFFECT OF AL, B AND TI ADDITION ON HIGH-TEMPERATURE STRENGTH OF 17CR-14NI-2.5MO HEAT RESISTING CAST STEEL
    HIYAMA, K
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1985, 71 (05): : S617 - S617
  • [33] A comparison of the dry sliding wear of single-phase f.c.c. carbon-doped Fe40.4Ni11.3Mn34.8Al7.5Cr6 and CoCrFeMnNi high entropy alloys with 316 stainless steel
    Guo, Xiaobin
    Baker, Ian
    Kennedy, Francis E.
    Ringer, Simon P.
    Chen, Hansheng
    Zhang, Weidong
    Liu, Yong
    Song, Min
    MATERIALS CHARACTERIZATION, 2020, 170
1234