Fabrication of carbon nanotube reinforced Al composites with well-balanced strength and ductility

被引：0
|
作者：
机构：
[1] [2,Yang, Xudong
[2] Liu, Enzuo
[3] Shi, Chunsheng
[4] He, Chunnian
[5] Li, Jiajun
[6] 1,Zhao, Naiqin
[7] Kondoh, Katsuyoshi
来源：
Zhao, N. (nqzhao@tju.edu.cn) | 1600年 / Elsevier Ltd卷 / 563期
关键词：
An approach was developed to fabricate carbon nanotube (CNT)-reinforced Al composites. In a typical process; the Co catalyst was evenly deposited on the surface of Al powder by impregnation route; and then the CNTs were grown in the Al powder by chemical vapor deposition to obtain CNT/Al powders. After ball-milling of the obtained powders for a short time; the CNT/Al composites were fabricated by compacting; sintering and hot extrusion of the ball-milled powders. During this process; the well dispersed CNT reinforcement is deeply embedded in the Al powder forming an effective interface bonding with matrix. As a result; the CNT/Al composites containing 2.5 wt.% CNTs exhibit the ultimate tensile strength of 334 MPa which is 1.7 times higher than that of unreinforced Al; and good ductility of ∼18% elongation to failure. Thus; well-balanced strength and ductility are achieved in CNT-reinforced Al composites.© 2013 Elsevier B.V. All rights reserved;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Journal article (JA)
引用
收藏
相关论文
共 50 条
  • [31] The fabrication and characterization of high density polyethylene composites reinforced by carbon nanotube coated carbon fibers
    Hu, Chao
    Liao, Xinwen
    Qin, Qing-Hua
    Wang, Gang
    COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2019, 121 : 149 - 156
  • [32] Fabrication and electromagnetic interference shielding effectiveness of carbon nanotube reinforced carbon fiber/pyrolytic carbon composites
    Liu, Xingmin
    Yin, Xiaowei
    Kong, Luo
    Li, Quan
    Liu, Ye
    Duan, Wenyan
    Zhang, Litong
    Cheng, Laifei
    Carbon, 2014, 68 : 501 - 510
  • [33] Achieving well-balanced strength and ductility via dual nanoscale precipitate structures in Co-free high-entropy alloys
    Liu, X. X.
    Ma, S. G.
    Wang, J. J.
    Zhao, D.
    Jiao, Z. M.
    Zhang, T. W.
    Qiao, L.
    Chen, X. Z.
    Wang, Z. H.
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2024, 29 : 5539 - 5549
  • [34] Effects of grafting strength and density on interfacial shear strength of carbon nanotube grafted carbon fibre reinforced composites
    Deng, Yan
    Islam, Mohammad S.
    Tong, Liyong
    COMPOSITES SCIENCE AND TECHNOLOGY, 2018, 168 : 195 - 202
  • [35] Progress in Fabrication Technique of Carbon Nanotubes Reinforced Al Matrix Composites
    Wu Chun
    Ma WenXin
    Chen YaPing
    Yan, LiYing Chen
    Li Jing
    PROCEEDINGS OF THE 2015 INTERNATIONAL CONFERENCE ON MATERIALS, ENVIRONMENTAL AND BIOLOGICAL ENGINEERING, 2015, 10 : 73 - 76
  • [36] Acquiring well balanced strength and ductility of Cu/CNTs composites with uniform dispersion of CNTs and strong interfacial bonding
    Wang, Xinhua
    Guo, Baisong
    Ni, Song
    Yi, Jianhong
    Song, Min
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2018, 733 : 144 - 152
  • [37] Achieving Well-Balanced Strength and Ductility in Warm-Rolled Fe-30.5Mn-8Al-1.0C Lightweight Austenitic Steels via Aging Treatment
    Zhang, Feng
    Chen, Peng
    Wang, Pengfei
    Li, Xiaowu
    ADVANCED ENGINEERING MATERIALS, 2024, 26 (22)
  • [38] Carbon fiber/carbon nanotube reinforced hierarchical composites: Effect of CNT distribution on shearing strength
    Zhou, H. W.
    Mishnaevsky, L., Jr.
    Yi, H. Y.
    Liu, Y. Q.
    Hu, X.
    Warrier, A.
    Dai, G. M.
    COMPOSITES PART B-ENGINEERING, 2016, 88 : 201 - 211
  • [39] Investigation of microstructure and wear behaviors of al matrix composites reinforced by carbon nanotube
    Yildirim, Musa
    Ozyurek, Dursun
    Guru, Metin
    FULLERENES NANOTUBES AND CARBON NANOSTRUCTURES, 2016, 24 (07) : 467 - 473
  • [40] Superplastic deformation behavior of carbon nanotube reinforced 7055 Al alloy composites
    Bi, S.
    Liu, Z. Y.
    Yu, B. H.
    Wu, L. H.
    Xiao, B. L.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2020, 797
12345