Synthesis of polycarbosilane with a super high molecule weight and its characterization

被引：0
|
作者：
College of Aerospace and Materials Engineering, National University of Defence Technology, Changsha 410073, China [1 ]
机构：
来源：
Huagong Xiandai | 2006年 / 6卷 / 48-50期
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
By the orthogonal design strategy, PCS with a super high molecule weight was synthesized under high pressure from the PCS with a low/middle molecule weight synthesized under normal pressure. Through research by FT-IR, GPC and NMR, its' structure and performance were characterised. It was found that PCS with a super high molecule weight could be synthesized under high pressure from the PCS with a low/middle molecule weight synthesized under normal pressure. Suitable reaction time should be 6 hours at 460°C to 470°C and under 1 MPa to 2 MPa beforehand. Average molecule weight of the as-synthesized PCS was 6400 to 8500. Both its' degree of branching and the content of Si-H decreased. The average molecule weight of PCS with a super high molecule weight could be better adjusted by means of adjustment of reaction time.
引用
收藏
相关论文
共 50 条
  • [31] Synthesis of super high molecular weight sodium polyacrylate by inverse suspension polymerization
    Zhao, Chun-Feng
    Liu, Kun-Yuan
    Han, Shu-Zhen
    Beijing Huagong Daxue Xuebao(Ziran Kexueban)/Journal of Beijing University of Chemical Technology, 2002, 29 (01):
  • [32] Synthesis of high molecular weight PPS and its properties
    Park, LS
    Lee, SC
    Lee, TH
    Jeon, JY
    POLYMER-KOREA, 1997, 21 (03) : 369 - 374
  • [33] Research on synthesis of polycarbosilane at high temperature under high pressure and vacuum distillation
    Xie, Zheng-Fang
    Cheng, Xiang-Zhen
    Song, Yong-Cai
    Xiao, Jia-Yu
    Guofang Keji Daxue Xuebao/Journal of National University of Defense Technology, 2006, 28 (02): : 39 - 43
  • [34] Synthesis and characterization of molybdenum-modified polycarbosilane for SiC(Mo) ceramics
    Xie, Zhengfang
    Niu, Jiaxin
    Chen, Zhaohui
    JOURNAL OF APPLIED POLYMER SCIENCE, 2013, 128 (03) : 1834 - 1841
  • [35] Synthesis and characterization of continuous freestanding silicon carbide films with polycarbosilane (PCS)
    Yao, Rongqian
    Feng, Zude
    Yu, Yuxi
    Li, Siwei
    Chen, Lifu
    Zhang, Ying
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2009, 29 (10) : 2079 - 2085
  • [36] Synthesis and characterization of super-high surface MCM-41.
    Song, CM
    Yan, ZF
    ABSTRACTS OF PAPERS OF THE AMERICAN CHEMICAL SOCIETY, 2002, 223 : A69 - A69
  • [37] Synthesis and characterization of super absorbent polymers for high-mechanical output
    Chen, R. L.
    Chen, B. C.
    Liao, T.
    Goldberg, I. B.
    Chen, C. L.
    SIXTEENTH INTERNATIONAL CONFERENCE ON ADAPTIVE STRUCTURES AND TECHNOLOGIES, 2006, : 3 - 10
  • [38] Synthesis and characterization of high molecular weight polyaniline/MWNTs composites
    Chao, DM
    Chen, JY
    Lu, XF
    Chen, L
    Zhang, WJ
    CHEMICAL JOURNAL OF CHINESE UNIVERSITIES-CHINESE, 2005, 26 (11): : 2176 - 2178
  • [39] Synthesis and characterization of novel high molecular weight silsesquioxanes.
    Rahimian, K
    Loy, DA
    Wheeler, DR
    ABSTRACTS OF PAPERS OF THE AMERICAN CHEMICAL SOCIETY, 1998, 215 : U419 - U419
  • [40] Synthesis and characterization of high molecular weight poly(trimethylene oxide)
    Qureshi, MY
    Ochel, M
    EUROPEAN POLYMER JOURNAL, 1996, 32 (06) : 691 - 693
12345