Structure evolution and thermal stability of SMAT-derived nanograined layer on Ti-25Nb-3Mo-3Zr-2Sn alloy at elevated temperatures

被引：0

作者：

机构：

[1] Huang, Run

[2] Han, Yong

来源：

Han, Y. (yonghan@mail.xjtu.edu.cn) | 1600年 / Elsevier Ltd卷 / 554期

关键词：

A nanocrystalline layer; which consists of pure β phase with average grain size of about 30 nm on Ti-25Nb-3Mo-3Zr-2Sn alloy; was fabricated by surface mechanical attrition treatment (SMAT). The microstructure evolution; phase transitions and thermal stability of the nanocrystalline layer during isochronal annealing at temperatures of 300-600 °C were investigated by XRD and TEM. During annealing; the nanocrystalline layer underwent recovery; recrystallization and significant grain growth. Recovery occurs at temperatures from 300 to 400 °C resulting in strain relaxation; dislocation annihilation and a very limited growth of β grains dominated by re-ordering of grain boundaries (GBs). α Precipitates start to precipitate along the β GBs at 350 °C; which exhibit equiaxed morphology with size less than 10 nm. Recrystallization proceeds at a higher temperature up to 450 °C leading to a reduction of β grain size. Due to the pinning effect of the α precipitates; β grains sizes can be maintained less than 100 nm until the annealing temperature increased to 550 °C; e.g; 0.41 Tm (melting temperature in K); above which significant grain growth occurs to overstep nanocystalline scale; and the growth activation energy of β grains is calculated as 40.8 kJ/mol. The abnormal low value is caused by the nonequilibrium GBs of β grains in the as-SMATed surface layer; which increase atomic mobility even in the presence of pinning effect of the α precipitates on the β GBs. © 2012 Elsevier B.V. All rights reserved;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Journal article (JA)

引用

共 50 条

[31] An In Vitro Evaluation of the Hierarchical Micro/Nanoporous Structure of a Ti3Zr2Sn3Mo25Nb Alloy after Surface Dealloying
Wang, Lan
Zhou, Wenhao
Yu, Zhentao
Yu, Sen
Zhou, Lian
Cao, Yemin
Dargusch, Matthew
Wang, Gui
ACS APPLIED MATERIALS & INTERFACES, 2021, 13 (13) : 15017 - 15030
[32] Pseudoelastic behaviour of a β Ti-25Nb-3Zr-3Mo-2Sn alloy (vol 527, pg 2246, 2010)
Kent, D.
Wang, G.
Yu, Z.
Dargusch, M. S.
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2010, 527 (16-17): : 4524 - 4524
[33] Fine Grain Surface on Biomechanics Compatibility of Ti3Zr2Sn3Mo25Nb
Jin H.
Shen W.
Xu J.
Cao X.
Wang Q.
Xiyou Jinshu/Chinese Journal of Rare Metals, 2022, 46 (09): : 1190 - 1198
[34] Microstructure and wear resistance of Ti-3Zr-2Sn-3Mo-15Nb(TLM) alloy
于振涛
郑玉峰
牛金龙
皇甫强
张亚峰
余森
Transactions of Nonferrous Metals Society of China, 2007, (S1) : 495 - 499
[35] Study on the Preparation and Corrosion-Wear Properties of TiN/Sn Coatings on the Ti-25Nb-3Zr-2Sn-3Mo Titanium Alloy
Pu, Jiang
Dai, Yan
Li, Kunmao
Chen, Li
MATERIALS, 2025, 18 (05)
[36] Microstructure and wear resistance of Ti-3Zr-2Sn-3Mo-15Nb (TLM) alloy
Yu Zhen-Tao
Zheng Yu-Feng
Niu Jin-Long
Huangfu Qiang
Zhang Ya-Feng
Yu Sen
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2007, 17 : S495 - S499
[37] In situ scanning electron microscopy observation of deformation and fracture behavior of Ti-3Zr-2Sn-3Mo-25Nb alloy
Xiqun Ma
Zhentao Yu
Yong Han
Xiping Song
Qiaoyan Sun
Rare Metals, 2012, 31 : 318 - 322
[38] Preparation and osteoinduction of active micro-arc oxidation films on Ti-3Zr-2Sn-3Mo-25Nb alloy
Yu Sen
Yu Zhen-tao
Wang, Gui
Han Jian-ye
Ma Xi-qun
Dargusch, Matthew S.
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2011, 21 (03) : 573 - 580
[39] In situ scanning electron microscopy observation of deformation and fracture behavior of Ti-3Zr-2Sn-3Mo-25Nb alloy
Ma Xiqun
Yu Zhentao
Han Yong
Song Xiping
Sun Qiaoyan
RARE METALS, 2012, 31 (04) : 318 - 322
[40] In situ scanning electron microscopy observation of deformation and fracture behavior of Ti-3Zr-2Sn-3Mo-25Nb alloy
MA Xiqun a
RareMetals, 2012, 31 (04) : 318 - 322

← 1 2 3 4 5 →