Microstructure response and LBE corrosion behavior of the FeCrAlY coating after Au-ions irradiation

被引：0

作者：

Zhang, Wei ^{[1
]}

Deng, Jiuguo ^{[1
]}

Zhong, Yilong ^{[1
]}

Liu, Hao ^{[1
]}

Long, Ziyao ^{[2
]}

Wang, Rongshuo ^{[1
]}

Li, Yudong ^{[1
]}

Qu, Guofeng ^{[1
]}

Zhou, Mingyang ^{[2
]}

Yang, Jijun ^{[1
]}

机构：

[1] Sichuan Univ, Inst Nucl Sci & Technol, Key Lab Radiat Phys & Technol, Minist Educ, Chengdu 610064, Peoples R China

[2] Nucl Power Inst China, Sci & Technol Reactor Syst Design Technol Lab, Chengdu 610213, Peoples R China

来源：

CORROSION SCIENCE | 2024年 / 241卷

基金：

中国国家自然科学基金;

关键词：

Au-ions irradiation; LBE corrosion; FeCrAlY coating; 550; DEGREES-C; MECHANICAL-PROPERTIES; POINT-DEFECTS; LEAD ALLOY; CLAM STEEL; T91; RESISTANCE; OXIDATION; AL; TRANSPORT;

D O I：

10.1016/j.corsci.2024.112521

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The microstructure and LBE corrosion behavior of the irradiated (up to 110 dpa) Fe15Cr11Al0.5Y coatings were investigated. The surface roughness and hardness increased with the irradiation dose. Irradiation induces grain growth, and the grown grains contain many dislocations, but no segregation and voids. Irradiation accelerates the corrosion rate of the coating, and the irradiated coatings suffer from serious inward non-uniform growth of the Al2O3 layer. The reaction of Al2O3 with PbO promoted the formation of the outermost PbAl2O4 of the irradiated coating. A "competitive mechanism" was proposed to explain the evolution of the corrosion behavior of the irradiated coatings.

引用

页数：19

共 50 条

[31] Corrosion behavior of refractory TiNbZrMoV high-entropy alloy coating in static lead-bismuth eutectic alloy: A novel design strategy of LBE corrosion-resistant coating?
Deng, Jiuguo
Yang, Jian
Lv, Liangliang
Zhang, Wei
Chen, Qingsong
Zhou, Mingyang
Zhu, Changda
Liu, Ning
Yang, Jijun
SURFACE & COATINGS TECHNOLOGY, 2022, 448
[32] Effect of Au-ion irradiation on the corrosion behavior of CLF-1 steel
Bai, Fan
Zhang, Wei
Wang, Long
Feng, Yongjin
Feng, Kaiming
Liu, Ning
Yang, Jijun
FUSION ENGINEERING AND DESIGN, 2022, 183
[33] The influence of post treatments on the microstructure and corrosion behavior of thermally sprayed NiCrMoAl alloy coating
Daram, P.
Banjongprasert, C.
SURFACE & COATINGS TECHNOLOGY, 2020, 384
[34] Microstructure and Corrosion Behavior of Atmospheric Plasma Sprayed NiCoCrAlFe High Entropy Alloy Coating
Mehmood, Kashif
Umer, Malik Adeel
Munawar, Ahmed Umar
Imran, Muhammad
Shahid, Muhammad
Ilyas, Muhammad
Firdous, Rabeeka
Kousar, Humaira
Usman, Muhammad
MATERIALS, 2022, 15 (04)
[35] Microstructure and Corrosion Behavior of MAO-SG Composite Coating on 7075 Aluminum Alloy
Chen, X. W.
Cai, L. P.
Zhang, D. F.
Li, M. L.
Ran, Y.
Ping, W.
TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2022, 75 (11) : 2931 - 2938
[36] Microstructure and Corrosion Behavior of Cold-Sprayed Zn-Al Composite Coating
Zhao, Zhipo
Tang, Junrong
Tariq, Naeem ul Haq
Wang, Jiqiang
Cui, Xinyu
Xiong, Tianying
COATINGS, 2020, 10 (10) : 1 - 11
[37] Influence of aging treatment on microstructure, wear and corrosion behavior of a nickel base hardfaced coating
Kesavan, D.
Kamaraj, M.
WEAR, 2011, 272 (01) : 7 - 17
[38] Influence of W content on microstructure and corrosion behavior of laser cladded Inconel 718 coating
Sun, Pengfei
Wang, Dengzhi
Song, Wenji
Tang, Congwen
Yang, Jiaxing
Xu, Zhidong
Hu, Qianwu
Zeng, Xiaoyan
SURFACE & COATINGS TECHNOLOGY, 2023, 452
[39] Microstructure and High Temperature Corrosion Behavior of Wire-Arc Sprayed FeCrSiB Coating
Li, Ran
Zhou, Zheng
He, Dingyong
Wang, Yiming
Wu, Xu
Song, Xiaoyan
JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2015, 24 (05) : 857 - 864
[40] Microstructure and Corrosion Behavior of MAO-SG Composite Coating on 7075 Aluminum Alloy
X. W. Chen
L. P. Cai
D. F. Zhang
M. L. Li
Y. Ran
W. Ping
Transactions of the Indian Institute of Metals, 2022, 75 : 2931 - 2938

← 1 2 3 4 5 →