Ordering-facilitated lower hydrogen embrittlement sensitivity in a prototype high-entropy alloy

The ageing treatment (450 degrees C/60 h) led to the spinodal decomposition at grain boundaries (GBs) and the development of chemical short-range orders (CSROs) in the alloy matrix, increasing the strength and effectively reducing the hydrogen embrittlement (HE) sensitivity of the equiatomic FeMnNiCoCr alloy. Firstly, the emergence of NiMn- and Cr-rich orders at GB regions reduces hydrogen diffusion rates along GBs and limits hydrogen enrichment at these sites. Secondly, CSROs promote hydrogen accumulation within the grain interior and impede hydrogen penetration, resulting in a shallower hydrogen-affected depth in the aged sample. Moreover, the modulation of hydrogen distribution by microstructure initiates transgranular cracking in the aged sample.