Grain size and strength of the ni3al intermetallic compound synthesized under pressure

被引：0

作者：

Ovcharenko V. ^{[1
]}

Kozulin A. ^{[1
]}

Akimov K. ^{[1
]}

机构：

[1] Institute of Strength Physics and Materials Science SB RAS, Tomsk

来源：

Solid State Phenomena | 2021年 / 313卷

关键词：

Grain size; High-temperature synthesis; Intermetallic compound Ni[!sub]3[!/sub]Al; Pressure; Ultimate tensile strength;

D O I：

10.4028/www.scientific.net/SSP.313.41

中图分类号：

学科分类号：

摘要：

This paper presents the results of the investigation of the grain structure formation in the intermetallic compound Ni3Al under conditions of its high-temperature synthesis under pressure in a powder mixture of nickel and aluminum of stoichiometric composition and the effect of grain size on the strength properties of the synthesized intermetallic compound. The grain structure was investigated by optical metallography, transmission electron microscopy, and EBSD analysis; the ultimate tensile strength of the intermetallic compound was investigated under the tension of the samples in the temperature range from 20 to 1000 °C. It was found that with a decrease in the grain size, not only does the tensile strength of the intermetallic compound multiply increases but also on the anomalous temperature dependence of the intermetallic compound strength there is a significant shift in the maximum strength value to the region of higher temperatures. © 2021 Trans Tech Publications Ltd, Switzerland.

引用

页码：41 / 49

页数：8

共 50 条

[21] Hot deformation behaviour and grain refinement of intermetallic compound Ni3Al
VSB - Technical Univ of Ostrava, Ostrava - Poruba, Czech Republic
J Mater Process Technol, 1-4 (575-580):
[22] Hot deformation behaviour and grain refinement of intermetallic compound Ni3Al
Schindler, I
Machacek, J
Kliber, J
Greger, M
Kursa, M
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 1996, 60 (1-4) : 575 - 580
[23] GRAIN SIZE INFLUENCES THE CORROSION AND CAVITATION OF Ni3Al INTERMETALLIC ALLOYS
Zasada, D.
Jasionowski, R.
Sienkiewicz, J.
METALURGIJA, 2015, 54 (01): : 47 - 50
[24] The shock Hugoniot of the intermetallic compound Ni3Al
Knapp, I.
Millett, J. C. F.
Gray, G. T., III
Bourne, N. K.
Meziere, Y. J. E.
Shock Compression of Condensed Matter - 2005, Pts 1 and 2, 2006, 845 : 741 - 744
[25] Concentration heterogeneity in structure of Ni3Al intermetallic synthesized under compression
Perevalova, OB
Fedorischeva, MB
Ovcharenko, VE
Su, HH
JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2002, 18 (05) : 432 - 435
[26] SUPERDISLOCATION DISSOCIATION IN INTERMETALLIC COMPOUND Ni3Al
Mao Wen Present addresss: Institute of Materials Science
Transactions of Nonferrous Metals Society of China, 1999, (S1) : 95 - 99
[27] THE EFFECT OF GRAIN-SIZE ON THE YIELD STRENGTH OF NI3AL
SCHULSON, EM
WEIHS, TP
VIENS, DV
BAKER, I
ACTA METALLURGICA, 1985, 33 (09): : 1587 - 1591
[28] Self-diffusion of Ni in the intermetallic compound Ni3Al
Chen, Guo-Xiang
Wang, Dou-Dou
Zhang, Jian-Min
Huo, Han-Ping
Xu, Ke-Wei
PHYSICA B-CONDENSED MATTER, 2008, 403 (19-20) : 3538 - 3542
[29] Effect of alloying with hafnium and boron on the parameters of grain structure in the intermetallic compound Ni3Al
Perevalova, OB
PHYSICS OF METALS AND METALLOGRAPHY, 2005, 100 (02): : 172 - 178
[30] Infiltration and combustion synthesis of an intermetallic compound Ni3Al
Nakae, H
Fujii, H
Nakajima, K
Goto, A
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1997, 223 (1-2): : 21 - 28

← 1 2 3 4 5 →