The impact fretting corrosion behavior and damage mechanism of Inconel 690TT under different impact forces in high temperature pressurized water

被引：0
|
作者：
Bian, W. W. [1 ]
Lu, Y. H. [1 ]
Kang, L. Z. [1 ]
Zhang, X. F. [1 ]
Xin, L. [1 ]
Shoji, T. [1 ,2 ]
机构：
[1] Univ Sci & Technol Beijing, Natl Ctr Mat Serv Safety, Beijing 100083, Peoples R China
[2] Tohoku Univ, New Ind Creat Hatchery Ctr, Frontier Res Initiat, 6-6-10 Aramaki Aoba,Aoba Ku, Sendai, Miyagi 9808579, Japan
来源：
CORROSION SCIENCE | 2024年 / 240卷
基金：
中国国家自然科学基金;
关键词：
Inconel; 690; TT; Impact fretting corrosion; Oxidation; Microstructure; SURFACE OXIDE-FILMS; WEAR BEHAVIOR; DYNAMIC RECRYSTALLIZATION; NANOLAMINATED STRUCTURE; ALLOY; 690TT; DEFORMATION; TUBES; SUPERALLOY; EVOLUTION; DIFFUSION;
D O I：
10.1016/j.corsci.2024.112507
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The impact fretting corrosion of Inconel 690TT under different impact forces was investigated. The results indicated that there was a competitive relationship between formation of third body layer (TBL) and fragmentation of TBL caused by impact force. With the increase of impact forces, damage mechanism changed from adhesive wear to delamination wear, and crack initiation sites gradually shifted from TBL to internal oxidation zone in tribologically transformed structure (TTS) layer. Nanocrystalline boundaries and defects induced by impact force provided channels for internal oxidation. The formation mechanism of TTS was the combined effect of continuous dynamic recrystallization (cDRX) and twin-assisted cDRX.
引用
收藏
页数：19
相关论文
共 50 条
  • [21] CORROSION BEHAVIORS OF INCONEL 690TT AND INCOLOY 800MA STEAM GENERATOR TUBES IN HIGH TEMPERATURE HIGH PRESSURE WATER
    Wang Jianqiu
    Huang Fa
    Ke Wei
    ACTA METALLURGICA SINICA, 2016, 52 (10) : 1333 - 1344
  • [22] Cyclic deformation behavior and cracking mechanism of Inconel Alloy 690TT steam generator tube at elevated temperature
    Li, Z. H.
    Hong, C.
    Zhao, Y. G.
    Hu, Y.
    Lu, Y. H.
    Shoji, T.
    MATERIALS CHARACTERIZATION, 2022, 190
  • [23] Study on Fretting Wear of 690TT Alloy Heat Transfer Tube in High Temperature and High Pressure Water Environment
    Chu Q.
    Huang Q.
    Zhang M.
    Jiang Q.
    Tan W.
    Yuanzineng Kexue Jishu/Atomic Energy Science and Technology, 2023, 57 (10): : 1964 - 1971
  • [24] Surface Oxidation and Subsurface Microstructure Evolution of Alloy 690TT Induced by Partial Slip Fretting Corrosion in High-Temperature Pure Water
    Xin, Long
    Han, Yongming
    Ling, Ligong
    Lu, Yonghao
    Shoji, Tetsuo
    ACTA METALLURGICA SINICA-ENGLISH LETTERS, 2021, 34 (04) : 543 - 554
  • [25] Surface Oxidation and Subsurface Microstructure Evolution of Alloy 690TT Induced by Partial Slip Fretting Corrosion in High-Temperature Pure Water
    Long Xin
    Yongming Han
    Ligong Ling
    Yonghao Lu
    Tetsuo Shoji
    Acta Metallurgica Sinica (English Letters), 2021, 34 : 543 - 554
  • [26] Microstructure Evolution of 690 TT Heat Transfer Tube Under Impact Slip Dual-Axis Fretting Corrosion in High Temperature and High Pressure Water Environment
    Zhou, Bokai
    Liu, Xin
    Li, Shen
    Hu, Yong
    RARE METAL MATERIALS AND ENGINEERING, 2024, 53 (08) : 2156 - 2166
  • [27] Surface Oxidation and Subsurface Microstructure Evolution of Alloy 690TT Induced by Partial Slip Fretting Corrosion in High-Temperature Pure Water
    Long Xin
    Yongming Han
    Ligong Ling
    Yonghao Lu
    Tetsuo Shoji
    ActaMetallurgicaSinica(EnglishLetters), 2021, 34 (04) : 543 - 554
  • [28] The synergy of corrosion and fretting wear process on Inconel 690 in the high temperature high pressure water environment
    Wang, Zihao
    Xu, Jian
    Li, Jie
    Xin, Long
    Lu, Yonghao
    Shoji, Tetsuo
    Takeda, Yoichi
    Otsuka, Yuichi
    Mutoh, Yoshiharu
    JOURNAL OF NUCLEAR MATERIALS, 2018, 502 : 255 - 262
  • [29] Effects of foreign object damage on high-cycle fatigue behavior of Inconel Alloy 690TT steam generator tubes
    Li, Z. H.
    Lu, Y. H.
    Hong, C.
    Zhao, Y. G.
    Zhang, W. D.
    Shoji, T.
    ENGINEERING FRACTURE MECHANICS, 2023, 292
  • [30] Electrochemical study on the fretting corrosion synergistic damage mechanism of Inconel 690 alloy in different dissolved oxygen solution
    Zhang, Shengzan
    Liu, Liyan
    Bonzom, Remy
    Mi, Xue
    Tan, Wei
    Zhu, Guorui
    ELECTROCHIMICA ACTA, 2024, 474
12345