Study on fracture mechanism of low-circle fatigue in rapidly solidified Al-Li alloy

被引：0
|
作者：
Yuan, S.Q.
Bai, Y.J.
Ai, S.H.
机构：
来源：
Liaoning Gongcheng Jishu Daxue Xuebao (Ziran Kexue Ban)/Journal of Liaoning Technical University (Natural Science Edition) | 2001年 / 20卷 / 01期
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
引用
收藏
相关论文
共 50 条
  • [41] Low cycle fatigue resistance of Al-Li alloys
    Prasad, NE
    Rao, PR
    MATERIALS SCIENCE AND TECHNOLOGY, 2000, 16 (04) : 408 - 426
  • [42] The corrosion behaviors and mechanism of 1420 Al-Li alloy
    Cui, YS
    Zhu, ZY
    Liu, S
    Ke, W
    Zhang, Y
    Zhang, WM
    SCRIPTA MATERIALIA, 1996, 34 (05) : 781 - 786
  • [43] THE STRUCTURE AND PROPERTIES OF A RAPIDLY SOLIDIFIED AL-MG-LI ALLOY
    WANG, W
    GRANT, NJ
    INTERNATIONAL JOURNAL OF RAPID SOLIDIFICATION, 1985, 1 (02): : 157 - 171
  • [44] FATIGUE-CRACK GROWTH IN 2090 AL-LI ALLOY
    PAO, PS
    COOLEY, LA
    IMAM, MA
    YODER, GR
    SCRIPTA METALLURGICA, 1989, 23 (08): : 1455 - 1460
  • [45] FATIGUE BEHAVIOR OF THE AL-LI ALLOY 8090 COMPARED TO 2024
    PETERS, M
    BACHMANN, V
    WELPMANN, K
    ZEITSCHRIFT FUR WERKSTOFFTECHNIK-MATERIALS TECHNOLOGY AND TESTING, 1987, 18 (08): : 277 - 283
  • [46] Microstructural characterization and fatigue properties of 2195 Al-Li alloy
    Chaturvedi, M. C.
    Chen, D. L.
    ALUMINIUM ALLOYS 2006, PTS 1 AND 2: RESEARCH THROUGH INNOVATION AND TECHNOLOGY, 2006, 519-521 : 147 - 152
  • [47] Fatigue-crack growth in 2090 Al-Li alloy
    Pao, P.S., 1600, (23):
  • [48] FATIGUE CRACK-GROWTH OF AL-LI ALLOY 2090
    PAO, PS
    IMAM, MA
    COOLEY, LA
    YODER, GR
    JOURNAL OF METALS, 1988, 40 (11): : 63 - 63
  • [49] Effect and mechanism of Li content on the corrosion resistance of Al-Li alloy
    Han, Chao
    Yu, Mei
    Xiao, Jian
    Yang, Zhong
    Zhao, Zhenjiang
    Jia, Xuejiao
    Li, Songmei
    Liu, Jianhua
    CORROSION SCIENCE, 2025, 246
  • [50] HYDROGEN-INDUCED FRACTURE IN A RSP AL-LI ALLOY
    ZHEN, L
    YANG, DZ
    YU, GF
    HOU, SE
    SCRIPTA METALLURGICA ET MATERIALIA, 1994, 31 (05): : 595 - 599
12345