Influence of Nb diffusion layer on superconductivity of MgB2/Nb/Cu wires

被引：0

作者：

机构：

[1] [1,2,3,Wang, Qingyang

[2] 1,Zhang, Pingxiang

[3] Yan, Guo

[4] 3,Sulpice, A.

[5] Xiong, Xiaomei

[6] Yang, Fang

[7] Liu, Guoqing

[8] Jiao, Gaofeng

[9] Li, Chengshan

来源：

Li, C. (MgB2@QQ.com) | 1600年 / Science Press卷 / 42期

关键词：

Diffusion barriers - Niobium compounds - Magnesium compounds - Heat treatment - Wire - Copper compounds;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

The MgB2 wires were prepared by in-situ Powder-in-Tube (PIT) method with Nb/Cu compounds tube as the sheath and then were heat treated at various temperatures for 2 h in flowing argon. The resistivity (R-T), magnetic moment (M-T), transport critical current (Ic-B) and magneto optical (MO) properties of MgB2 wires were analyzed. The results show that there is a diffusion layer between MgB2 superconducting core and Nb barrier layer when the heat-treatment temperature is higher than 750°C, and this diffusion layer obstructs the current transfer into MgB2 superconductor core from the Cu sheath. This indicates that the best heat-treatment temperature for the MgB2 wires with Nb as the barrier layer should be lower than 750°C. Copyright © 2013 Northwest Institute for Nonferrous Metal Research. Published by Elsevier BV. All rights reserved.

引用

共 50 条

[41] Superconductivity in MgB2
Dai, W
Feng, QR
Gao, ZX
PROGRESS IN NATURAL SCIENCE-MATERIALS INTERNATIONAL, 2002, 12 (11) : 801 - 807
[42] Superconductivity in MgB2
Akimitsu, J
Muranaka, T
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2003, 388 : 98 - 102
[43] Structural Defects of Superconducting Core of the Single Fiber MgB2/Nb,Cu Composite
Kuznetsova, E. I.
Krinitsina, T. P.
Blinova, Yu. V.
Degtyarev, M. V.
Konovalov, P. V.
Dikhtiyevskaya, K. K.
Abdyukhanov, I. M.
Tsapleva, A. S.
PHYSICS OF METALS AND METALLOGRAPHY, 2024, 125 (08): : 878 - 886
[44] AC Loss Properties Of Cu-Sheathed MgB2 Composites With Nb Barriers
Funaki, Kazuo
Sueyoshi, Takahiro
Kajikawa, Kazuhiro
Iwakuma, Masataka
Tanaka, Kazuhide
Okada, Michiya
Kumakura, Hiroaki
Hayashi, Hidemi
8TH EUROPEAN CONFERENCE ON APPLIED SUPERCONDUCTIVITY (EUCAS'07), 2008, 97
[45] Fabrication of 6-filament MgB2 wires enhanced by high strength 91-filament Cu-Nb composite
Sun, Yu Yan
Zhang, Ping Xiang
Sulpice, Andre
Mossang, Eric
Liang, Ming
Yan, Guo
JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS, 2013, 24 (04) : 1250 - 1255
[46] Influence of iridium doping in MgB2 superconducting wires
Grivel, J. -C.
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2018, 547 : 7 - 15
[47] Microstructure and superconductivity of Cu addition MgB2 wires using Mg2Cu compound as additional source material
Hishinuma, Y.
Kikuchi, A.
Iijima, Y.
Yoshida, Y.
Takeuchi, T.
Nishimura, A.
SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2006, 19 (12): : 1269 - 1273
[48] Influence of microstructures and crystalline defects on the superconductivity of MgB2
Serquis, A
Liao, XZ
Zhu, YT
Coulter, JY
Huang, JY
Willis, JO
Peterson, DE
Mueller, FM
Moreno, NO
Thompson, JD
Nesterenko, VF
Indrakanti, SS
JOURNAL OF APPLIED PHYSICS, 2002, 92 (01) : 351 - 356
[49] MgB2 films on Nb substrate and its bending test
Yao, Dan
Zhuang, Chenggang
Li, Fen
Feng, Qingrong
Wang, Fu-ren
2006 BIMW: 2006 BEIJING INTERNATIONAL MATERIALS WEEK, PTS 1-4: MAGNESIUM, 2007, 546-549 : 2051 - +
[50] Properties of in situ made MgB2 in Nb or Ti sheath
Kovac, P.
Husek, I.
Kopera, L.
Melisek, T.
Rosova, A.
Dobrocka, E.
SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2013, 26 (02):

← 1 2 3 4 5 →