Fatigue behavior of powder metallurgy superalloy FGH97

被引：0

作者：

Nai Q.-L. ^{[1
]}

Dong J.-X. ^{[1
]}

Zhang M.-C. ^{[1
]}

Zheng L. ^{[1
]}

Yao Z.-H. ^{[1
]}

机构：

[1] School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing

来源：

Gongcheng Kexue Xuebao/Chinese Journal of Engineering | 2016年 / 38卷 / 02期

关键词：

Fatigue crack growth rate; Hafnium; Nickel base superalloys; Powder metallurgy;

D O I：

10.13374/j.issn2095-9389.2016.02.014

中图分类号：

学科分类号：

摘要：

The fatigue crack growth rates of powder metallurgy (P/M) superalloy FGH97 with different grain sizes, γ' phase sizes and Hf contents were measured at a 650℃ high temperature condition and compared with those of FGH95 and FGH96 alloys. The fatigue fracture behavior characteristic of FGH97 alloy in each stage was analyzed by the quantitative analysis method. It is found that FGH97 alloy with coarser grains has a lower fatigue crack growth rate. Reasonable match of secondary and tertiary γ' phases and Hf addition can get a higher fatigue life. Compared with FGH95 and FGH96 alloys, FGH97 alloy has the highest fatigue cack intiation resistance and exihibits the lowest fatigue crack propagation rate at high temperature. © All right reserved.

引用

页码：248 / 256

页数：8

共 15 条

[11] Zhang M.J., Li F.G., Wang S.Y., Et al., Effect of powder preparation technology on the hot deformation behavior of HIPed P/M nickel-base superalloy FGH96, Mater Sci Eng A, 528, 12, (2011)
[12] Zhang L.N., Dong J.X., Microstructures' effects on high temperature fatigue failure behavior of typical superalloys, Mater Sci Eng A, 587, (2013)
[13] Xu J., Zhang G.P., Effects of grain size and initial immobile dislocation density on fatigue behavior of polycrystalline metals, Mater Sci Eng A, 590, (2014)
[14] Yang J., Dong J.X., Zhang M.C., Et al., High temperature fatigue crack growth behavior of a novel powder metallurgy superalloy FGH98, Acta Metall Sin, 49, 1, (2013)
[15] Wang P., Dong J.X., Zhang Y.W., Effect of time aging treatment on the γ' phase evolution of FGH97 P/M supperalloy, Rare Met Mater Eng, 43, 5, (2014)

← 1 2 →