Ionic conductivity of glass-ceramic composites in the AgI-Ag2O-V2O5 system

被引:0
|
作者
机构
[1] Krasowski, K.
[2] Garbarczyk, J.E.
[3] Wasiucionek, M.
来源
Krasowski, K. | 2001年 / Wiley-VCH Verlag Berlin GmbH, Weinheim, Germany卷 / 183期
关键词
Annealing - Ceramic materials - Composition - Crystallization - Glass - Glass transition - Ionic conduction in solids - Silver compounds - Temperature - Ternary systems - Thermodynamic stability - X ray diffraction analysis;
D O I
暂无
中图分类号
学科分类号
摘要
Electrical ionic conductivity of two families of silver-vanadate superionic glass-ceramic composites: 50 AgI &middot (50 - x)Ag2O &middot xV2O5, 14 &le x &le 25 and y AgI &middot (80 - y)Ag2O &middot 20 V2O5, 30 &le y &le 50 was studied. The composites were prepared by annealing initially amorphous samples of the above compositions at temperatures slightly exceeding their crystallization temperatures Tc. The formation of crystallites was evidenced by X-ray diffraction patterns of the annealed samples. The structural changes induced by the annealing were closely correlated with the modifications of ionic conductivity. The conductivity of the obtained composites was, at elevated temperatures, higher than that of the original glasses. Moreover it did not change (within hours) at stabilized temperatures exceeding glass transition temperature while the conductivity of the glasses was thermally stable only below Tg. The highest measured value of σ (0.1 S/cm at 150°C) is close to those found in the best superionic conductors at these temperatures.
引用
收藏
相关论文
共 50 条
  • [31] Impedance spectroscopy of Na2S-V2O5-P2O5 glass-ceramic nanocomposites
    Wally, N. K.
    Sheha, E.
    Kamal, B. M.
    Ali, Atif M.
    Ali, A. M.
    El-Desoky, M. M.
    JOURNAL OF NON-CRYSTALLINE SOLIDS, 2022, 598
  • [32] Enhancement in conductivity by K2O in MgO-V2O5 glass-ceramic for solid- state battery application
    Dua, Vimi
    Singh, K.
    SOLID STATE IONICS, 2024, 417
  • [33] Effect of nanocrystallization on electrical conductivity of glasses and composites of the AgI-Ag2O-B2O3 system
    Foltyn, M
    Wasiucionek, M
    Garbarczyk, J
    Nowinski, JL
    SOLID STATE IONICS, 2005, 176 (25-28) : 2137 - 2140
  • [34] Effect of conditional glass former variation on electrical transport in Li2O-P2O5 glassy and glass-ceramic ionic system
    Rathore, Munesh
    Dalvi, Anshuman
    SOLID STATE IONICS, 2014, 263 : 119 - 124
  • [35] Glass structure of the Ag2O-TeO2-V2O5 system
    Dimitriev, Y
    Ivanova, Y
    Dimitrova, M
    Lefterova, ED
    Angelov, PV
    JOURNAL OF MATERIALS SCIENCE LETTERS, 2000, 19 (17) : 1513 - 1516
  • [36] Electrical properties of AgI-Ag2O-V2O5-P2O5 glasses
    Garbarczyk, JE
    Machowski, P
    Wasiucionek, M
    Jakubowski, W
    SOLID STATE IONICS, 2003, 157 (1-4) : 269 - 273
  • [37] Cyclic electrical conductivity in BaTiO3-PbTiO3-V2O5 glass-ceramic nanocomposite
    Bahgat, A. A.
    Heikal, Sh.
    Mahdy, Iman A.
    Abd-Rabo, A. S.
    Ghany, A. Abdel
    PHYSICA B-CONDENSED MATTER, 2014, 447 : 23 - 29
  • [38] Electrical transport in Li2SO4-Li2O-P2O5 ionic glasses and glass-ceramic composites: A comparative study
    Rathore, Munesh
    Dalvi, Anshuman
    SOLID STATE IONICS, 2013, 239 : 50 - 55
  • [39] Preparation of glass-ceramic in Li2O-Al2O3-GeO2-P2O5 system
    Nikolic, Jelena D.
    Smiljanjic, Sonja V.
    Matijasevic, Srdan D.
    Zivanovic, Vladimir D.
    Tosic, Mihajlo B.
    Grujic, Snezana R.
    Stojanovic, Jovica N.
    PROCESSING AND APPLICATION OF CERAMICS, 2013, 7 (04) : 147 - 151
  • [40] MIXED GLASS FORMER EFFECT IN AGI-AG-2O-V-2O-5-P-2O-5 QUATERNARY AMORPHOUS SOLID ELECTROLYTES
    PRASAD, PSS
    RANI, AND
    RADHAKRISHNA, S
    MATERIALS CHEMISTRY AND PHYSICS, 1990, 25 (05) : 487 - 499