Influence of temperature, cyclic frequency, and steel strength on surface fatigue crack growth behavior of low and high carbon steel wires in sea water

被引：0
|
作者：
Suzuki, Yohnosuke [1 ]
Motoda, Shin-Ichi [1 ]
Ito, Fumio [1 ]
Tsujikawa, Shigeo [1 ]
机构：
[1] Toba Natl. Coll. of Mar. Technology, 1-1, Ikegami-cho, Toba 517-8501, Japan
来源：
Zairyo to Kankyo/ Corrosion Engineering | 2002年 / 51卷 / 11期
关键词：
D O I：
10.3323/jcorr1991.51.502
中图分类号：
学科分类号：
摘要：
21
引用
收藏
页码：502 / 509
相关论文
共 50 条
  • [21] INFLUENCE OF SURFACE REINFORCEMENT ON FATIGUE-STRENGTH OF LOW-CARBON STEEL
    LUTHER, RG
    WILLIAMS, TR
    METALLURGIA AND METAL FORMING, 1974, 41 (03): : 72 - 77
  • [22] Fatigue crack growth in welds of high strength microalloyed steel
    Hidvéghy, J
    Bursák, M
    Michel, J
    METALURGIJA, 1999, 38 (01): : 19 - 23
  • [23] Fatigue crack growth behavior in stainless steel under cyclic torsion
    Yu, Huichen
    Tanaka, Keisuke
    STRUCTURAL INTEGRITY AND MATERIALS AGEING IN EXTREME CONDITIONS, 2010, : 227 - 232
  • [24] Fatigue crack growth behavior in weld-repaired high-strength low-alloy steel
    Zhang, Chunguo
    van der Vyver, Stefan
    Hu, Xiaozhi
    Lu, Pengmin
    ENGINEERING FRACTURE MECHANICS, 2011, 78 (09) : 1862 - 1875
  • [25] FATIGUE CRACK-GROWTH IN HIGH AND LOW STRENGTH STEEL UNDER TORSIONAL LOADING
    TSCHEGG, EK
    THEORETICAL AND APPLIED FRACTURE MECHANICS, 1985, 3 (02) : 157 - 178
  • [26] The influence of partial surface shot peening on fatigue crack growth behaviour of a high-strength ferritic steel
    Al-Turaihi, A.
    Mehmanparast, A.
    Brennan, F.
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2018, 41 (03) : 663 - 674
  • [27] Effect of pits on fatigue strength of carbon steel in oxygenated high temperature water
    Kanasaki, H
    Tsutsumi, K
    Kondo, Y
    LOCALIZED DAMAGE IV: COMPUTER-AIDED ASSESSMENT AND CONTROL, 1996, : 623 - 630
  • [28] Effect of water environment on fatigue-crack growth of low-alloy high-strength steel
    Matocha, K
    Tvrdy, M
    Pahuta, P
    Hyspecká, L
    KOVOVE MATERIALY-METALLIC MATERIALS, 1999, 37 (03): : 200 - 208
  • [29] Fatigue Crack Growth Behavior in Pipes and Elbows of Carbon Steel and Stainless Steel Materials\
    Arora, Punit
    Singh, P. K.
    Bhasin, V.
    Vaze, K. K.
    Pukazhendhi, D. M.
    Gandhi, P.
    Raghava, G.
    6TH INTERNATIONAL CONFERENCE ON CREEP, FATIGUE AND CREEP-FATIGUE INTERACTION, 2013, 55 : 703 - 709
  • [30] Effect of test frequency on fatigue strength of low carbon steel
    Tsutsumi, N.
    Murakami, Y.
    Doquet, V.
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2009, 32 (06) : 473 - 483
12345