Effect of phosphorus distribution on stress rupture properties of a low thermal expansion superalloy

被引：0

作者：

Sun, Yaru ^{[1
,2
]}

Sun, Wenru ^{[2
]}

Sun, Xiaofeng ^{[2
]}

Guo, Shouren ^{[2
]}

Liu, Zheng ^{[1
]}

Hu, Zhuangqi ^{[2
]}

机构：

[1] School of Materials Science and Engineering, Shenyang University of Technology, Shenyang 110023, China

[2] Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China

来源：

Cailiao Yanjiu Xuebao/Chinese Journal of Materials Research | 2008年 / 22卷 / 03期

关键词：

Grain boundaries - Precipitation (chemical) - Superalloys;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

The behavior of phosphorus in the Thermo-Span alloy in which the addition of Al and Cr was modified was studied. The phosphorus bearing phase was observed both in the grain interior and at the grain boundaries when the alloy was solutioned at 1093C. The phosphorus bearing phase was largely dissolved when the alloy was solutioned at 1160C, leaving only a small amount in the grain interior. The influence of phosphorus on the stress rupture properties was determined by the existing state of phosphorus in the alloy. Phosphorus largely reduced the stress rupture life when it caused the precipitation of the phosphorus-bearing phase, while it increased the stress rupture life of the alloys when it was concentrated at the defects such as grain boundaries or dislocations.

引用

页码：235 / 240

共 50 条

[41] Development of a low thermal expansion, crack growth resistant superalloy
Smith, JS
Heck, KA
SUPERALLOYS 1996, 1996, : 91 - 100
[42] Effect of β-aging on microstructure and mechanical properties of low expansion superalloy GH783
National Key Laboratory of Advanced High Temperature Structural Materials, Institute of Aeronautical Materials, Beijing 100095, China
Jinshu Rechuli, 2007, 9 (31-33):
[43] Stability of microstructure and stress-rupture properties of IN792 superalloy
Yang, Jinxia
Zheng, Qi
Sun, Xiaofeng
Hu, Zhuangqi
Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2012, 41 (06): : 1038 - 1040
[44] Stability of Microstructure and Stress-rupture Properties of IN792 Superalloy
Yang Jinxia
Zheng Qi
Sun Xiaofeng
Hu Zhuangqi
RARE METAL MATERIALS AND ENGINEERING, 2012, 41 (06) : 1038 - 1040
[45] Evaluation of the Lifetime and Effect of Furnace Thermal Cycling on Stress Rupture Behaviour of a Thermal Barrier Coated Superalloy Used in a Turbine Blade
Ray, A. K.
Bose, S. C.
De, P. K.
Das, H. K.
Mandal, D.
Alam, H. Z.
Sharma, V. S. R. A.
Das, D. K.
CANADIAN METALLURGICAL QUARTERLY, 2010, 49 (02) : 191 - 204
[46] Existence Form and Distribution of Mn and the Effect of Mn Content on High-Temperature Stress Rupture Properties of K417G Superalloy
Yang Yaqian
Xing Weiwei
Chen Weiliang
Chen Bo
Ma Yingche
Liu Kui
RARE METAL MATERIALS AND ENGINEERING, 2021, 50 (10) : 3470 - 3476
[47] Effect of minor additions on the microstructures and stress rupture properties of a directionally solidified Ni-based superalloy
Zhang, H. W.
Qin, X. Z.
Li, X. W.
Zhou, L. Z.
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2018, 711 : 303 - 312
[48] Effect of Re Content on Mircrostructure and Stress Rupture Properties of DD15 Single Crystal Superalloy
Shi, Zhenxue
Liu, Shizhong
Yue, Xiaodai
Wang, Zhicheng
Li, Jiarong
Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2023, 52 (06): : 1977 - 1984
[49] Effect of Re Content on Mircrostructure and Stress Rupture Properties of DD15 Single Crystal Superalloy
Shi Zhenxue
Liu Shizhong
Yue Xiaodai
Wang Zhicheng
Li Jiarong
RARE METAL MATERIALS AND ENGINEERING, 2023, 52 (06) : 1977 - 1984
[50] Effect of Hf Content on the Microstructures and Stress Rupture Properties of DD6 Single Crystal Superalloy
Shi Zhenxue
Li Jiarong
Liu Shizhong
Luo Yushi
Zhao Jinqian
RARE METAL MATERIALS AND ENGINEERING, 2010, 39 (08) : 1334 - 1338

← 1 2 3 4 5 →