Observation of surface microstructure of tricalcium silicate by transmission electron microscopy

被引：0
|
作者：
Hisa, Masaaki [1 ]
Sembiring, Nelson [1 ]
Shirakami, Tatsuya [1 ]
Urabe, Kazuyori [1 ]
机构：
[1] Fac. Sci. and Technol., Mat. Chem., Ryukoku University, 1-5, Yokotani, Seta Oe-cho, Otsu-shi 520-2194, Japan
来源：
Nippon Seramikkusu Kyokai Gakujutsu Ronbunshi/Journal of the Ceramic Society of Japan | 2000年 / 108卷 / 1264期
关键词：
Amorphous films - Crystal microstructure - Electron beams - Electron irradiation - Ethanol - Hydration - Lime - Transmission electron microscopy - X ray diffraction analysis;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The surface microstructure of tricalcium silicate (C3S) was observed by transmission electron microscopy (TEM). The tricalcium silicate specimen was dispersed in ethanol or isopropanol. It was then placed on a copper mesh with a collodion film that had an amorphous layer on the surface of each grain. The amorphous layer was caused by the hydration reaction of C3S with water in the dispersants. The irradiation by an electron beam caused the layer to change into CaO crystallites with a concurrent formation of silica-rich domains.