Intrinsic coercivity of SmCo based permanent magnetic films prepared on hot substrates at 650℃

被引：0

作者：

Li, Yuanxun ^{[1
]}

Peng, Long ^{[2
]}

机构：

[1] State Key Laboratory of Electronic Thin Films and Integrated Devices, University of Electronic Science and Technology of China, Chengdu,610054, China

[2] Chengdu University of Information Technology, Chengdu,610225, China

来源：

Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering | 2015年 / 44卷 / 04期

关键词：

Chromium - Cobalt alloys - Coercive force - Metallic films - Temperature distribution - Binary alloys - Film preparation - Substrates - Film thickness - Rare earths - Samarium alloys - Molybdenum - Magnetism - Magnetic multilayers;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

The intrinsic coercivity of the SmCo based permanent magnetic films prepared on the hot Si substrate at 650℃ with Al, Cu, Ag, Mo, and Cr underlayer without a subsequent annealing process was investigated. The results show that the films with Mo and Cr underlayer provide an improved intrinsic coercivity. The film thickness presents a complex effect on the intrinsic coercivity of the films with Mo underlayer. When the film thickness is 3.0 µm, the maximum value of the intrinsic coercivity is 281.6 kA·m-1 at room temperature. Furthermore, the temperature dependence of intrinsic coercivity is found to be strongly correlated with the magnetic parameters. In the range from 25℃ to 300℃, the intrinsic coercivity of the films of above 200 kA·m-1 is obtained. Copyright © 2015, Northwest Institute for Nonferrous Metal Research. Published by Elsevier BV. All rights reserved.

引用

页码：796 / 799

共 50 条

[21] Magnetic Properties and Coercivity of MnGa Films Deposited on Different Substrates
Feng, J. N.
Liu, W.
Gong, W. J.
Zhao, X. G.
Kim, D.
Choi, C. J.
Zhang, Z. D.
JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2017, 33 (03) : 291 - 294
[22] Magnetic Properties of SmCo7 Permanent Magnetic Films for High Temperature Applications
Peng Long
Tu Xiaoqiang
Li Lezhong
Wang Rui
RARE METAL MATERIALS AND ENGINEERING, 2014, 43 (10) : 2335 - 2338
[23] Hard magnetic SmCo thin films prepared by pulsed laser deposition
Neu, V
Thomas, J
Fähler, S
Holzapfel, B
Schultz, L
JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2002, 242 : 1290 - 1293
[24] Microstructure and properties of SmCo(Al, Si)/Cr permanent in magnetic thin films
Wang, X.
Li, Z.
Lin, G.
Cai, C.
2001, Huazhong University of Science and Technology (29):
[25] Microstructure and Magnetic Anisotropy of SmCo-Based Films Prepared via External Magnetic Field Assisted Magnetron Sputtering
Li, Hao
Wei, Lu
Hong, Yuan
Zhang, Yuanwei
Qiu, Zhaoguo
Wang, Gang
Zhao, Lizhong
Liu, Xiaolian
Zhang, Xuefeng
Chen, Deyang
Zheng, Z. G.
Xia, Weixing
Zeng, Dechang
Liu, J. Ping
ADVANCED ENGINEERING MATERIALS, 2023, 25 (05)
[26] Structure, magnetic properties, and coercivity mechanism of nanocomposite SmCo5/α-Fe magnets prepared by mechanical milling
Zhang, J
Zhang, SY
Zhang, HW
Shen, BG
JOURNAL OF APPLIED PHYSICS, 2001, 89 (10) : 5601 - 5605
[27] Evolution of magnetic domain structures and coercivity in high-performance SmCo 2:17-type permanent magnets
Gutfleisch, O
Müller, KH
Khlopkov, K
Wolf, M
Yan, A
Schäfer, R
Gemming, T
Schultz, L
ACTA MATERIALIA, 2006, 54 (04) : 997 - 1008
[28] Effects of temperature gradients on magnetic anisotropy of SmCo based films
Wei, L.
Zhang, Y. W.
Gong, Y. S.
Hong, Y.
Qiu, Z. G.
Zhao, L. Z.
Liu, X. L.
Zhang, X. F.
Chen, D. Y.
Zheng, Z. G.
Xia, W. X.
Zeng, D. C.
Dempsey, N. M.
Liu, J. P.
JOURNAL OF ALLOYS AND COMPOUNDS, 2022, 898
[29] Strategy of preparing SmCo based films with high coercivity and remanence ratio achieved by temperature and chemical optimization
Yansong Gong
Zhaoguo Qiu
Sizhe Liang
Xinrui Zheng
Hongxia Meng
Zhigang Zheng
Deyang Chen
Shengfu Yuan
Weixing Xia
Dechang Zeng
JPLiu
JournalofRareEarths, 2024, 42 (07) : 1289 - 1297
[30] Fully in plane aligned SmCo based films prepared by pulsed laser deposition
Cadieu, FJ
Rani, R
Theodoropoulos, T
Chen, L
JOURNAL OF APPLIED PHYSICS, 1999, 85 (08) : 5895 - 5897

← 1 2 3 4 5 →