Study of the tribological behavior of B4C reinforced MoSi2 based composites

被引：0
|
作者：
Yan, Feng-Yuan [1 ]
Lin, Xin-Hua [1 ]
Lu, Jin-Jun [1 ]
Qi, Shang-Kui [1 ]
机构：
[1] Lab. of Solid Lubrication, Lanzhou Inst. of Chem. Phys., Chinese Acad. of Sci., Lanzhou 730000, China
来源：
Mocaxue Xuebao/Tribology | 2002年 / 22卷 / 04期
关键词：
Boron compounds - Friction - Molybdenum compounds - Oxidation - Reinforcement - Wear resistance;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
B4 particles-reinforced MoSi2-based composites were prepared by rapid heat compression molding. The influence of the B4C particle content on the microstructure, mechanical properties and tribological behavior of MoSi2-based composites was investigated. The results show that with the increase of B4C particle content, the hardness of the composite is increased, while the friction coefficient and the wear rate are decreased. It is supposed that B4C particles can retard the oxidation of MoSi2N, preventing the formation of glass phase between crystals and improving the interface combination of crystals. The tribochemical product is also beneficial for the modification of the tribological properties of B4C particles-reinforced MoSi2-based composites.
引用
收藏
页码：263 / 267
相关论文
共 50 条
  • [21] Oxidation behaviour of particle reinforced MoSi2 composites at temperatures up to 1700 °C -: Part II:: Initial screening of the oxidation behaviour of MoSi2 composites
    Lohfeld, S
    Schütze, M
    Böhm, A
    Güther, V
    Rix, R
    Scholl, R
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2005, 56 (03): : 149 - 158
  • [22] Oxidation behaviour of particle reinforced MoSi2 composites at temperatures up to 1700°C.: Part III:: Oxidation behaviour of optimised MOSi2 composites
    Lohfeld, S
    Schütze, M
    Böhm, A
    Güther, V
    Rix, R
    Scholl, R
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2005, 56 (04): : 250 - 258
  • [23] Investigation of Mechanical Behavior of Stir Casted Al Based Composites Reinforced With B4C Nanoparticles
    Alizadeh, Ali
    Taheri-nassaj, Ehsan
    Hajizamani, Mohsen
    MANUFACTURING SCIENCE AND TECHNOLOGY, PTS 1-8, 2012, 383-390 : 2728 - +
  • [24] Effect of B4C, MoSi2, nano SiC and micro-sized SiC on pressureless sintering behavior, room-temperature mechanical properties and fracture behavior of Zr(Hf)B2-based composites
    Abdollahi, Alireza
    Mashhadi, Mehri
    CERAMICS INTERNATIONAL, 2014, 40 (07) : 10767 - 10776
  • [25] MECHANICAL AND TRIBOLOGICAL BEHAVIOUR OF B4C REINFORCED AlSi12-XMg MATRIX COMPOSITES
    Cevik, E.
    Sun, Y.
    JOURNAL OF THE BALKAN TRIBOLOGICAL ASSOCIATION, 2015, 21 (04): : 725 - 735
  • [26] 热压过程中MoSi2与B4C的反应研究
    李建林
    江东亮
    谭寿洪
    金属学报, 1999, (06) : 634 - 637
  • [27] In-situ reinforced MoSi2 composites by mechanical alloying
    Jayashankar, S.
    Kaufman, M.J.
    Scripta metallurgica et materialia, 1992, 27 (08): : 1245 - 1250
  • [28] Fabrication and Tribological Behavior of Stir Cast Mg/B4C Metal Matrix Composites
    Amandeep Singh
    Niraj Bala
    Metallurgical and Materials Transactions A, 2017, 48 : 5031 - 5045
  • [29] Fracture characterization of MOSi2 based composites
    Lee, SP
    Jin, JO
    Park, JS
    Lee, JK
    Min, BH
    Yoon, HK
    Park, JY
    ADVANCES IN FRACTURE AND FAILURE PREVENTION, PTS 1 AND 2, 2004, 261-263 : 1481 - 1486
  • [30] Combustion synthesis of MoSi2 based composites
    Subrahmanyam, J
    INORGANIC MATRIX COMPOSITES, 1996, : 207 - 225
12345