Effect of Phosphorous Calcined Gypsum on Shrinkage Characteristics of Calcium Sulfoaluminate Cement Clinker

被引：0
|
作者：
Huang H. [1 ,2 ]
Liao Y. [1 ,3 ]
Jiang G. [1 ]
Liao G. [1 ,3 ]
Mei J. [1 ,3 ]
机构：
[1] School of Urban Construction, Wuhan University of Science and Technology, Wuhan
[2] China First Metallurgical Group Company Limited, Wuhan
[3] Institute of High Performance Engineering Structure, Wuhan University of Science and Technology, Wuhan
来源：
Jianzhu Cailiao Xuebao/Journal of Building Materials | 2022年 / 25卷 / 09期
关键词：
autogenous shrinkage; chemical shrinkage; drying shrinkage; internal relative humidity; phosphorous calcined gypsum（PCG）;
D O I：
10.3969/j.issn.1007-9629.2022.09.002
中图分类号：
学科分类号：
摘要：
The setting time， chemical shrinkage， autogenous shrinkage， internal relative humidity and drying shrinkage of calcium sulfoaluminate （CSA） cement clinker blended with different amounts of phosphorous calcined gypsum （PCG） were investigated. The results show that the setting time of paste is shortened significantly with the increase of PCG content， and the rate of chemical shrinkage and the internal relative humidity of the paste is decreased gradually. The autogenous shrinkage has a good relationship with the internal relative humidity of the paste. The stable stage of chemical shrinkage is accelerated when the content of PCG is not more than 25%. When the content of PCG is 25% to 30%, the CSA cement paste expanded during the autogenous shrinkage test and the drying shrinkage of CSA cement clinker pastes are less than the control sample. © 2022 Tongji University. All rights reserved.
引用
收藏
页码：893 / 900
页数：7
相关论文
共 28 条
  • [11] GUO Dawei, Effect of steel slag on the hydration and shrinkage characteristics of calcium sulfoaluminate cement［D］, (2020)
  • [12] WANG Yanmou, SU Muzhen, ZHANG Liang, Sulphoaluminate cement ［M］, (1999)
  • [13] HAN Jianguo, YAN Peiyu, Influence of lithium compound on sulphoaluminate cement hydration process［J］, Journal of the Chinese Ceramic Society, 38, 4, (2010)
  • [14] WEI Xiaosheng, Kinetics of structure formation and properties of concrete by electrical resistivity measurement, (2016)
  • [15] LIANG Xuhui, Fang LIU, Yaowen XU, Study on modification of hemihydrate phosphogypsum with ordinary Portland cement and its hydration mechanism［J］, Non‑Metallic Mines, 41, 2, (2018)
  • [16] QIAN Jueshi, YU Jincheng, SUN Huaqiang, Formation and function of ettringite in cement hydrates［J］, Journal of the Chinese Ceramic Society, 45, 11, (2017)
  • [17] CHRISTENSEN A N, JENSEN T R, HANSON J C, Formation of ettringite， Ca<sub>6</sub>Al<sub>2</sub>（SO<sub>4</sub>）<sub>3</sub>（OH）<sub>12</sub>∙26H<sub>2</sub>O， AFt， and monosulfate， Ca<sub>4</sub>Al<sub>2</sub>O<sub>6</sub>（SO<sub>4</sub>）∙14H<sub>2</sub>O， AFm‑14， in hydrothermal hydration of Portland cement and of calcium aluminum oxide‑calcium sulfate dihydrate mixtures studied by in situ synchrotron X‑ray powder diffraction［J］, Journal of Solid State Chemistry, 177, (2004)
  • [18] HARGIS C W, TELESCA A, MONTERIRO P J M, Calcium sulfoaluminate （Ye'elimite） hydration in the presence of gypsum［J］, Cement and Concrete Research, 65, pp. 15-20, (2014)
  • [19] GLASSER F P, ZHANG L, High‑performance cement matrices based on calcium sulfoaluminate‑belite compositions［J］, Cement and Concrete Research, 31, 12, (2001)
  • [20] Jiaping LIU, TIAN Qian, Early age deformation and shrinkage crack control of modern concrete［M］, (2020)
123