Influence of strain rate on fracture characteristics and diffusible hydrogen of high tensile steel under hydrogen charging

被引：0
|
作者：
Kitahara, Gaku [1 ]
Tsuji, Aya [1 ,3 ]
Asada, Takashi [1 ]
Suzuki, Tomohiro [1 ]
Horikawa, Keitaro [2 ]
Kobayashi, Hidetoshi [2 ]
机构：
[1] Toyota Central R and D Labs., Inc., Material and Processing Dept. Ⅰ, Japan
[2] Osaka University, Graduate School of Engineering Science, Department of Mechanical Science, Bioengineering, Division of Nonlinear Mechanics, Japan
[3] 41-1 Yokomichi, Nagakute,4801192, Japan
来源：
Zairyo to Kankyo/ Corrosion Engineering | 2019年 / 68卷 / 02期
关键词：
22;
D O I：
10.3323/jcorr.68.46
中图分类号：
学科分类号：
摘要：
引用
收藏
页码：46 / 52
相关论文
共 50 条
  • [21] Tensile Properties of an Electrolytically Hydrogen Charged Duplex Stainless Steel Affected by Strain Rate
    Yousefi, Afshin
    Itoh, Goroh
    ISIJ INTERNATIONAL, 2018, 58 (03) : 561 - 565
  • [22] HYDROGEN-ASSISTED CRACKING OF CR-MO STEEL IN SLOW STRAIN RATE TENSILE TEST WITH HIGH-PRESSURE GASEOUS HYDROGEN
    Matsunaga, Hisao
    Yoshikawa, Michio
    Kondo, Ryota
    Itoga, Hisatake
    Yamabe, Junichiro
    Matsuoka, Saburo
    ASME PRESSURE VESSELS AND PIPING CONFERENCE - 2015, VOL 6B, 2015,
  • [23] THE EFFECT OF STRAIN RATE ON THE STRAIN TO FRACTURE OF A SHEET STEEL UNDER BIAXIAL TENSILE-STRESS CONDITIONS
    BROOMHEAD, P
    GRIEVE, RJ
    JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME, 1982, 104 (02): : 102 - 106
  • [24] Effect of stain rate and hydrogen charging current on hydrogen embrittlement of carbon steel in high alkaline chloride environment
    Kobayashi M.
    Nishikata A.
    Tsuru T.
    Zairyo to Kankyo/ Corrosion Engineering, 2010, 59 (04): : 129 - 135
  • [25] Hydrogen damage of high tensile steel in concrete
    Abdel-Karim, R
    El-Raghy, SM
    Waheed, AF
    Swellam, MH
    CHEMISTRY AND ELECTROCHEMISTRY OF CORROSION AND STRESS CORROSION CRACKING: A SYMPOSIUM HONORING THE CONTRIBUTIONS OF R.W. STAEHLE, 2001, : 649 - 662
  • [26] Effect of tensile strain rate on spall fracture in 20 steel
    Laboratory for Shock Wave and Detonation Physics Research, Institute of Fluid Physics, China Academy of Engineering Physics, Mianyang 621900, China
    不详
    Baozha Yu Chongji, 2007, 3 (193-197):
  • [27] Study of the Hydrogen Delayed Fracture of Mooring Chain Steel using Strain Rate Testing
    Li, Songjie
    Sun, Panfei
    Yin, Jiang
    Wang, Maoqiu
    Wang, Chengduo
    Shao, Lixiang
    Li, Fan
    Li, Yuanyuan
    INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2019, 14 (09): : 9221 - 9230
  • [28] Effects of hydrogen on the mechanical response of X80 pipeline steel subject to high strain rate tensile tests
    Zheng, Yuanyuan
    Zhang, Lin
    Shi, Qiaoying
    Zhou, Chengshuang
    Zheng, Jinyang
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2020, 43 (04) : 684 - 697
  • [29] Study on fracture strain of Cr-Mo steel in high pressure hydrogen
    Ma, Kai
    Peng, Wenzhu
    Zheng, Jinyang
    Gu, Chaohua
    Zhang, Ruimin
    Liu, Yayu
    Hua, Zhengli
    INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2021, 46 (61) : 31501 - 31509
  • [30] THE INFLUENCE OF STRAIN RATE ON SOME TENSILE PROPERTIES OF STEEL
    CLARK, DS
    DUWEZ, PE
    PROCEEDINGS-AMERICAN SOCIETY FOR TESTING AND MATERIALS, 1950, 50 : 560 - 576
12345