Influence of strain rate on fracture characteristics and diffusible hydrogen of high tensile steel under hydrogen charging

被引：0
|
作者：
Kitahara, Gaku [1 ]
Tsuji, Aya [1 ,3 ]
Asada, Takashi [1 ]
Suzuki, Tomohiro [1 ]
Horikawa, Keitaro [2 ]
Kobayashi, Hidetoshi [2 ]
机构：
[1] Toyota Central R and D Labs., Inc., Material and Processing Dept. Ⅰ, Japan
[2] Osaka University, Graduate School of Engineering Science, Department of Mechanical Science, Bioengineering, Division of Nonlinear Mechanics, Japan
[3] 41-1 Yokomichi, Nagakute,4801192, Japan
来源：
Zairyo to Kankyo/ Corrosion Engineering | 2019年 / 68卷 / 02期
关键词：
22;
D O I：
10.3323/jcorr.68.46
中图分类号：
学科分类号：
摘要：
引用
收藏
页码：46 / 52
相关论文
共 50 条
  • [1] INFLUENCE OF HIGH-PRESSURE HYDROGEN ON FRACTURE CHARACTERISTICS OF STEEL
    VANNESS, HC
    STEINMAN, JB
    ANSELL, GS
    JOM-JOURNAL OF METALS, 1964, 16 (09): : 754 - &
  • [2] Slow strain rate tensile test results of new multiphase 17%Cr stainless steel under hydrogen cathodic charging
    Tavares, Sergio S. M.
    Bastos, Ivan N.
    Pardal, Juan M.
    Montenegro, Talles R.
    da Silva, M. R.
    INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2015, 40 (47) : 16992 - 16999
  • [3] Rapid evaluation of hydrogen embrittlement resistance for spot–welds of high tensile strength steel sheet by slow rate tensile shear test under hydrogen charging conditions
    Kitahara, Gaku
    Matsuoka, Hideaki
    Asada, Takashi
    Nippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals, 2021, 85 (02): : 75 - 83
  • [4] Rapid Evaluation of Hydrogen Embrittlement Resistance for Spot-Welds of High Tensile Strength Steel Sheet by Slow Rate Tensile Shear Test under Hydrogen Charging Conditions
    Kitahara, Gaku
    Matsuoka, Hideaki
    Asada, Takashi
    MATERIALS TRANSACTIONS, 2021, 62 (07) : 943 - 951
  • [5] Rapid Evaluation of Hydrogen Embrittlement Resistance for Spot-Welds of High Tensile Strength Steel Sheet by Slow Rate Tensile Shear Test under Hydrogen Charging Conditions
    Kitahara, Gaku
    Matsuoka, Hideaki
    Asada, Takashi
    JOURNAL OF THE JAPAN INSTITUTE OF METALS AND MATERIALS, 2021, 85 (02) : 75 - 83
  • [6] Hydrogen embrittlement of high strength steel under in situ corrosive charging conditions and tensile load
    Scharf, R.
    Muhr, A.
    Stellnberger, K. -H.
    Faderl, J.
    Holzer, C.
    Mori, G.
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2017, 68 (01): : 95 - 104
  • [7] EFFECTS OF STRAIN RATE AND MICROSTRUCTURE ON FRACTURE TOUGHNESS OF DUPLEX STAINLESS STEELS UNDER HYDROGEN CHARGING CONDITIONS
    Bahrami, Amir
    Bourgeon, Anais
    Cheaitani, Mohamad
    OMAE2011: PROCEEDINGS OF THE ASME 30TH INTERNATIONAL CONFERENCE ON OCEAN, OFFSHORE AND ARCTIC ENGINEERING, VOL 3: MATERIALS TECHNOLOGY, 2011, : 93 - 103
  • [8] Tensile failure of stainless-steel notched bars under hydrogen charging
    Valiente, A
    Toribio, J
    Cortes, R
    Caballero, L
    JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME, 1996, 118 (02): : 186 - 191
  • [9] Diffusible hydrogen behavior and delayed fracture of zinc-electrogalvanized high strength steel
    Suzuki, N
    Ishii, N
    Miyagawa, T
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1996, 82 (02): : 170 - 175
  • [10] SOME EFFECTS OF HYDROGEN ON THE DELAYED FRACTURE OF HIGH-TENSILE STEEL
    BELL, WA
    SULLY, AH
    JOURNAL OF THE IRON AND STEEL INSTITUTE, 1954, 178 (01): : 15 - 18
12345