The Influence of Temperature on Corrosion Resistance of Ti-Mo Alloy in Acidic Medium

被引:0
|
作者
Wei, Ya [1 ]
Fu, Yu [1 ]
Pan, Zhi-Min [1 ]
Wang, Xue-Fei [1 ]
Yu, Wei [2 ]
He, Shi-Lei [3 ]
Yuan, Qing-Ying [3 ]
Luo, Hong [1 ]
Li, Xiao-Gang [1 ]
机构
[1] Institute for Advanced Materials and Technology, Beijing,100083, China
[2] Institute of Engineering and Technology, University of Science and Technology Beijing, Beijing,100083, China
[3] CNPC Baoji Petroleum Steel Pipe Co., Ltd., Shaanxi, Baoji,721008, China
来源
Surface Technology | 2022年 / 51卷 / 09期
关键词
Binary alloys - Chlorine compounds - Corrosion resistance - Corrosion resistant alloys - Corrosive effects - Electrochemical corrosion - Electrochemical electrodes - Electrochemical impedance spectroscopy - Morphology - Oxide films - Pipeline corrosion - Scanning electron microscopy - Silver alloys - Silver halides - Temperature - Titanium alloys - Titanium oxides - X ray photoelectron spectroscopy;
D O I
暂无
中图分类号
学科分类号
摘要
Titanium alloy pipeline is playing an increasingly important role in petrochemical industry. This paper mainly explores the corrosion behavior of Ti-Mo alloy in 20wt.% HCl solution with different temperature changes, aiming at revealing the corrosion mechanism of Ti-Mo alloy and providing certain reference value for the application of Ti-Mo alloy in petrochemical industry. The titanium alloy used in this experiment is produced by CNPC Baoji Petroleum Steel Pipe Co., Ltd. The main components (wt.%) are as follows: 2.99 Mo, 0.60 Zr, 0.044 Fe, 0.014 C, 0.005 1 N, and the balance is Ti. X-ray diffraction (XRD) and Quanta 250 scanning electron microscope (SEM) were used to observe the phase and morphology of Ti-Mo alloy. Electrochemical test adopts typical three-electrode system, with saturated silver chloride electrode as reference electrode, platinum electrode as counter electrode, titanium alloy sample as working electrode with the area of 1 cm2. The electrochemical experiment temperature were 20, 30 50 and 70 °C. The potential range of polarization curve was ‒0.8 V (vs. Ag/AgCl) to 2 V (vs. Ag/AgCl) and the scanning frequency of electrochemical impedance spectroscopy (EIS) was 10−2 Hz to 105 Hz. The chemical composition of the oxide film was studied by 250Xi X-ray photoelectron spectroscopy. The oxide film was formed at 0.5 V (vs. Ref) for 7 200 s. Mott-Schottky was used to explore the properties of semiconductor films. The experimental frequency of Mott-Schottky was 1 000 Hz, the scanning potential was 2 to ‒1 V with the step size of 20 mV. 20wt.% HCl solution was selected as the static immersion test solution, and the temperature of the solution was kept at 20 °C, 30 °C, 50 °C and 70 °C respectively. After soaking for 15 days, ultrasonic cleaning with distilled water and alcohol, drying, weighing with a balance with accuracy of 0.1 mg, and observing the morphology after corrosion with 3D laser confocal and scanning electron microscope. The solution medium temperature produced a great influence on the corrosion behavior of Ti-Mo alloy. The corrosion potential decreased from ‒548.9 mV (vs. Ag/AgCl) to ‒593.3 mV (vs. Ag/AgCl) in the range of 20 to 70 °C. Ti-Mo alloys had the lowest corrosion current density at 20 °C, i. e., 36.925 μA/cm2, and the passive current density decreased as the temperature enhanced. In addition, the content of the oxide film had no obvious difference at various temperature, but the donor concentration in the film increased at elevated temperature. Besides, it caused the n-p type transition of the semiconductor characteristics. The corrosion rate of the Ti-Mo alloy in 20wt.% HCl solution were 1.138 3, 2.931 7, 35.217 and 39.838 6 mm/a when solution temperature were 20, 30, 50 and 70 °C, which indicated that the corrosion rate accelerated with the temperature went by. An increase in the temperature of the solution will promote the formation of defects and reduce the stability and corrosion resistance of the oxide film. The α and β phases form microgalvanic cells in the corrosion process, and the α phase is more prone to corrode acting as the anode, which is due to the higher content of Mo in the β phase. © 2022, Chongqing Wujiu Periodicals Press. All rights reserved.
引用
收藏
相关论文
共 50 条
  • [31] Influence of β-phase stability in elemental blended Ti-Mo and Ti-Mo-Zr alloys
    Mohan, Prakash
    Rajak, Dipen Kumar
    Pruncu, Catalin, I
    Behera, Ajit
    Amigo-Borras, Vicente
    Elshalakany, Abou Bakr
    MICRON, 2021, 142
  • [32] Influence of β-phase stability in elemental blended Ti-Mo and Ti-Mo-Zr alloys
    Mohan, Prakash
    Rajak, Dipen Kumar
    Pruncu, Catalin I.
    Behera, Ajit
    Amigó-Borrás, Vicente
    Elshalakany, Abou Bakr
    Micron, 2021, 142
  • [33] Influence of pore characteristics on microstructure, mechanical properties and corrosion resistance of selective laser sintered porous Ti-Mo alloys for biomedical applications
    Xie, Fangxia
    He, Xinbo
    Cao, Shunli
    Mei, Min
    Qu, Xuanhui
    ELECTROCHIMICA ACTA, 2013, 105 : 121 - 129
  • [34] Ti-Mo microalloyed medium Mn steels: Precipitation and strengthening mechanism
    Wang, S. Y.
    Wang, C. Z.
    Li, H. Y.
    Xu, D. F.
    Zhang, H. T.
    Xiao, N.
    Cai, M. H.
    Lee, Y. -k.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2024, 909
  • [35] Systematic Assessment of the Influence of Mo Concentration on the Oxygen Ingress in Ti-Mo System During High Temperature Oxidation
    Samimi, P.
    Brice, D. A.
    Ghamarian, I.
    Liu, Y.
    Collins, P. C.
    OXIDATION OF METALS, 2016, 85 (3-4): : 357 - 368
  • [36] Effect of Si on the Microstructure and Oxidation Resistance of Ti-Mo Alloys
    Jinming Ru
    Yuemei Wang
    Yuhua Zhou
    Ze Jiang
    Xiaojing Xu
    Jianwei Li
    JOM, 2020, 72 : 354 - 360
  • [37] Evaluation of mechanical properties and formability of metastable β-type Ti-Mo alloy
    Takemoto, Y
    Shimizu, I
    ADVANCES IN ENGINEERING PLASTICITY AND ITS APPLICATIONS, PTS 1 AND 2, 2004, 274-276 : 373 - 378
  • [38] INFLUENCE OF OMEGA-PHASE ON SUPERCONDUCTIVITY OF TI-MO ALLOYS
    HO, JC
    COLLINGS, EW
    PHYSICS LETTERS A, 1969, A 29 (04) : 206 - &
  • [39] In situ XRD study of dehydrogenation process of Ti-Mo alloy hydride
    Yuan Xuezhong
    Guo Xiumei
    Wu Erdong
    Wang Sucheng
    ACTA METALLURGICA SINICA, 2006, 42 (08) : 850 - 856
  • [40] Martensitic {332}<113> twin in beta type Ti-Mo alloy
    Takemoto, Y
    Hida, M
    Sakakibara, A
    JOURNAL OF THE JAPAN INSTITUTE OF METALS, 1996, 60 (11) : 1072 - 1078