HotdeformationbehaviorandmicrostructureevolutionofGH3536-TiB2compositesfabricatedbypowdermetallurgy<iclass="icon-zqcb"></i>

The hot deformation behavior and microstructure evolution of GH3536-TiB2composites fabricated by powder metallurgy（PM）were examined in the temperature range of 950–1150°C and strain rate range of 0.001–1 s-1. The hot compression stress-strain curves and the constitutive equation were obtained. In addition, the hot processing map was drawn, which indicated that the appropriate hot working window was 950–1050°C/0.001–0.1 s-1and 1050–1100°C/0.001–0.01 s-1. The microstructure analysis showed that the splitting and spheroidization of M3B2led to a decrease in size and volume fraction at 950–1100°C. At 1150°C,the eutectic microstructure of M3B2+ γ was formed due to the dissolution of M3B2, which caused macroscopic cracking of the deformed sample. Additionally, the deformation temperature and the strain rate had little effect on the size and volume fraction of M3B2. Besides, discontinuous dynamic recrystallization（DDRX） and continuous dynamic recrystallization（CDRX） were found in the deformed microstructure, while the former was dominant. Within the test range of this work, the dynamic recrystallization（DRX） fraction of the deformed composites was high due to the bulging nucleation of numerous interfaces. The DRX grain size increased with increasing deformation temperature or decreasing strain rate. Texture analysis showed that the deformation texture of <101>//compression direction RD existed in the matrix when the deformation temperature was below 1100°C, and the texture type became <001>//RD at 1100°C. Additionally, it was also found that the <001>//RD texture was formed in M3B2under the strain rates of 0.1 and 0.01 s-1.