Effect ff ect of NaCl Concentration on Galvanic Corrosion Behavior of Zinc and A1050 Couples

被引:0
|
作者
Jang, Junho [1 ]
Ooi, Azusa [1 ]
Tada, Eiji [1 ]
机构
[1] Tokyo Inst Technol, Sch Mat & Chem Technol, Dept Mat Sci & Engn, 2-12-1 Ookayama,Meguro Ku, Tokyo 1528552, Japan
关键词
Galvanic Current; Couple Potential; Zn/Al; Oxygen Reduction Reaction; ALUMINUM-STEEL; AL-ALLOYS; JOINTS;
D O I
10.5796/electrochemistry.24-00061
中图分类号
O646 [电化学、电解、磁化学];
学科分类号
081704 ;
摘要
In this study, effects of NaCl concentration on galvanic corrosion behavior of zinc and A1050 couple was investigated by means of corrosion potential and galvanic current measurements, surface observation, electrochemical impedance measurements, and polarization tests. Corrosion potential and galvanic currents were measured for 72 hours during immersion in 0.01 to 2 mol L-1 NaCl solutions. During the galvanic corrosion tests, the corrosion potential of the couples remained nearly constant, except in the early stage of immersion, and became more negative as the NaCl concentration increased. During the immersion test, the galvanic current always flowed in the direction of the zinc being the anode. However, the galvanic current changed with immersion time. That is, in the early stage of immersion, the galvanic currents were higher at higher NaCl concentrations, but over time, these values decreased, and after 72 hours, they decreased to much lower values and were almost independent of the NaCl concentration. Surface observations, electrochemical impedance measurements, and polarization curve measurements revealed that a decrease in the cathodic reaction rate on the A1050 surface with immersion time. Finally, the corrosion mechanisms that explain the galvanic corrosion of zinc and A1050 were discussed.
引用
收藏
页数:9
相关论文
共 50 条
  • [21] Electrochemical corrosion behavior of nanocrystalline zinc coatings in 3.5% NaCl solutions
    Mou Cheng Li
    Li Li Jiang
    Wen Qi Zhang
    Yu Hai Qian
    Su Zhen Luo
    Jia Nian Shen
    Journal of Solid State Electrochemistry, 2007, 11 : 1319 - 1325
  • [22] Corrosion behavior of sintered zinc-aluminum coating in NaCl solution
    Chen, L
    Li, N
    Zhou, DR
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2002, 12 (06) : 1214 - 1217
  • [23] Electrochemical corrosion behavior of nanocrystalline zinc coatings in 3.5% NaCl solutions
    Li, Mou Cheng
    Jiang, Li Li
    Zhang, Wen Qi
    Qian, Yu Hai
    Luo, Su Zhen
    Shen, Jia Nian
    JOURNAL OF SOLID STATE ELECTROCHEMISTRY, 2007, 11 (09) : 1319 - 1325
  • [24] Corrosion behavior of sintered zinc-aluminum coating in NaCl solution
    陈玲
    李宁
    周德瑞
    TransactionsofNonferrousMetalsSocietyofChina, 2002, (06) : 1214 - 1217
  • [25] The Effect of Flow Rate and NaCl Concentration on the Corrosion Behavior of Carbon Steel in NaCl Solutions Containing H2S
    Rachmawati, Indah Dwi
    Nurdin, Isdiriayani
    Widiatmoko, Pramujo
    Devianto, Hary
    Irmayanti, Festi
    Saptohadi, Samuel
    26TH REGIONAL SYMPOSIUM ON CHEMICAL ENGINEERING (RSCE 2019), 2020, 778
  • [26] Effect of concentration of hyaluronic acid and NaCl on corrosion behavior of 316L austenitic stainless steel
    Bansod, Ankur V.
    Khobragade, Nilay N.
    Giradkar, Karansagar V.
    Patil, Awanikumar P.
    MATERIALS RESEARCH EXPRESS, 2017, 4 (11):
  • [27] The effect of synthetic zinc corrosion products on corrosion of electrogalvanized steel. II. Zinc reactivity and galvanic coupling zinc/steel in presence of zinc corrosion products
    Yoo, J. D.
    Ogle, K.
    Volovitch, P.
    CORROSION SCIENCE, 2014, 83 : 32 - 37
  • [28] Effects of NaCl Concentration and Solution Temperature on the Galvanic Corrosion between CFRP and AA7075T6
    Hur, S. Y.
    Kim, K. T.
    Yoo, Y. R.
    Kim, Y. S.
    CORROSION SCIENCE AND TECHNOLOGY-KOREA, 2020, 19 (02): : 75 - 81
  • [29] Galvanic corrosion behavior of DU-2A12 aluminium alloy couple in 3.5%NaCl solution
    Wang, Qingfu
    Pu, Zhen
    Shuai, Maobing
    Lang, Dingmu
    Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2014, 43 : 393 - 396
  • [30] Galvanic Corrosion Behavior of DU-2A12 Aluminium Alloy Couple in 3.5%NaCl Solution
    Wang Qingfu
    Pu Zhen
    Shuai Maobing
    Lang Dingmu
    RARE METAL MATERIALS AND ENGINEERING, 2014, 43 : 393 - 396