Synergistic Leaching of Titanium, Aluminum, and Magnesium Components during Dilute Acid Pressure Treatment of High-Titanium Blast Furnace Slag

This study focuses on an improved leaching process through the combination of pressurized conditions and direct filtration of acid leaching slurry, which is conductive to improving the filterability of acid leaching systems and the extraction rates of Ti, Al, and Mg components. The effects of sulfuric acid concentration, reaction temperature, particle size of materials, acid-slag ratio, and reaction time on the leaching efficiency were systematically investigated. The results showed that pressurization significantly enhances the filtration efficiency of the reaction slurry. Under the same filtration time, the filtration efficiency increased from 46% under ordinary pressure to 78% under pressurized conditions. Moreover, under the optimal reaction conditions, the extraction rates of Ti, Al, and Mg components were more than 88.21%, 97.8%, and 96.31%, respectively. Additionally, XRD and FTIR showed that titanium oxide sulfate hydrate crystals were produced in the acid-leached residues when the reaction temperature exceeded 190 degrees C, thereby reducing the extraction rate of Ti component. And the XRD pattern shows that when the reaction temperature is maintained at 190 degrees C and the reaction time is extended to 150 min, titanium oxide sulfate hydrate crystals will be formed to reduce the extraction rate of the Ti component. In summary, this study not only provides important theoretical support for the resource utilization of high-titanium blast furnace slag but also offers a feasible solution for efficient extraction and convenient filtration, thus holding significant academic and practical implications.