The Influence of Pore-Forming Diluents on Porous Structure, Thermal and Sorption Properties of the Divinylbenzene and Glycidyl Methacrylate Copolymers

The aim of this work was the characterization of polymer microspheres obtained by the suspension polymerization of divinylbenzene (DVB) and glycidyl methacrylate (GMA), depending on the pore-forming diluents and molar ratio of monomers. The assessed properties included the chemical and porous structure, thermal stability, and sorption capacity of the obtained polymers towards methylene blue. The abovementioned characteristic was carried out for two series of copolymers with molar ratios of monomers of 1:2, 1:1 and 2:1, synthetized with toluene and a mixture of decanol and benzyl alcohol. The structure of the polymers was confirmed by FTIR and elemental analysis. The results of TGA demonstrated the main influence on thermal stability was the composition of polymers, whereas the impact of porogens was negligible. The S-BET varied in the range of 12-534 m(2)g(-1) for polymers obtained with toluene and 0-396 m(2)g(-1) with the mixture of alcohols. Toluene enhanced the formation of micro- and mesopores, while the mixture of alcohols enhanced the creation of meso- and macropores. For the polymers prepared with toluene, their effectiveness in water purification decreases in the following order: DVB-GMA 2:1 > DVB-GMA 1:1 > DVB-GMA 1:2, according to the decreasing values of porous structure parameters. In the case of a series obtained with a mixture of alcohols, such correlation was not observed.