Effect of Polytetrafluoroethylene Coating on Corrosion Wear Properties of AZ31 Magnesium Alloy by Electrophoretic Deposition

In this study, we aim to enhance the corrosion and wear resistance of AZ31 magnesium alloy using electrophoretic deposition (EPD) technology to apply a hydrophobic polytetrafluoroethylene (PTFE) coating. Polyethyleneimine (PEI) serves as a charged dispersant, facilitating uniform deposition of PTFE particles on the alloy surface. Results demonstrate a significant reduction in corrosion current density (from 67.5 mu A/cm2 to 5.2 mu A/cm2) and improved wear resistance (wear volume decreased from 0.24167 mm3 to 0.00167 mm3) in a 3.5 wt% NaCl solution compared to uncoated alloy. Moreover, the friction coefficient of the coated sample decreases. These findings underscore the potential of nano-PTFE coatings prepared via EPD in enhancing AZ31 magnesium alloy's corrosion and wear resistance, providing a foundation for future protective coating design and optimization.