An Ultramicroporous Graphene-Based 3D Structure Derived from Cellulose-Based Biomass for High-Performance CO2 Capture

The use of powered activated carbon is often limited by inconsistent particle sizes and porosities, leading to reduced adsorption efficiencies. In this study, we demonstrated a practical and environmentally friendly method for creating a 3D graphene nanostructure with highly uniform ultramicropores from wood-based biomass through a series of delignification, carbonization, and activation processes. In addition, we evaluated the capture characteristics of this structure for CO2, CH4, and N-2 gases as well as its selectivity for binary-mixture gases. Based on textural and chemical analyses, the delignified monolith had a lamellar structure interconnected by cellulose-based fibers. Interestingly, applying the KOH vapor activation technique solely to the delignified samples led to the formation of a monolithic 3D network composed of interconnected graphene sheets with a high degree of crystallinity. Especially, the Act. 1000 sample exhibited a specific surface area of 1480 m(2)/g and a considerable pore volume of 0.581 cm(3)/g, featuring consistently uniform ultramicropores over 90% in the range of 3.5-11 & Aring;. The monolithic graphene-based samples, predominantly composed of ultramicropores, demonstrated a notably heightened capture capacity of 6.934 mol/kg at 110 kPa for CO2, along with favorable selectivity within binary gas mixtures (CO2/N-2, CO2/CH4, and CO2/CH4). Our findings suggest that this biomass-derived 3D structure has the potential to serve as a monolithic adsorbent in gas separation applications.