Experimental Analysis of HSLA Steel Welded Joint Fracture Behaviour

被引：0
|
作者：
Milovic, Ljubica [1 ]
Sedmak, Aleksandar [2 ]
Blacic, Ivo
Vuherer, Tomaz
Petrovski, Blagoj
机构：
[1] Univ Belgrade, Fac Technol & Met, Karnegijeva 4, Belgrade 11120, Serbia
[2] Univ Belgrade, Fac Mech Engn, Kraljice Marije 16, Belgrade 11120, Serbia
来源：
23 EUROPEAN CONFERENCE ON FRACTURE, ECF23 | 2022年 / 42卷
关键词：
HSLA; SEM micrographs; welding; fracture; PLANE-STRAIN; CRACK; RESISTANCE; IMPACT; PARAMETERS; TOUGHNESS; WELDMENTS;
D O I：
10.1016/j.prostr.2022.12.190
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
In order to assess the integrity of welded pressure vessel containing a crack, the behavior of three-point bending specimens made of HSLA steel welded joint are tested at -40 degrees C, and their fracture behaviour analyzed, as a conservative measure of crack resistance. Specimens were made of low-alloyed steel NIONIKRAL 70, welded by SAW process. Surface notches were machined by the electro-erosion method in the parent metal (PM), heat affected zone (HAZ) and weld metal (WM). The highest resistance to cracking was in PM, and the lowest one in WM, due to so-called pop-in behaviour. (c) 2022 The Authors. Published by Elsevier B.V.
引用
收藏
页码：1497 / 1502
页数：6
相关论文
共 50 条
  • [41] Evaluation of cold crack susceptibility on HSLA steel welded joints
    Silverio-Freire, RC
    Moura-Maciel, T
    da Silva, PG
    REVISTA DE METALURGIA, 2003, 39 (02) : 83 - 89
  • [42] Analysis of dynamic fracture and crack arrest of an HSLA steel in an SE(T) specimen
    United States Naval Academy, Annapolis, MD 21402
    J. ASTM Int., 2006, 1 (63-88):
  • [43] Analysis of dynamic fracture and crack arrest of an HSLA steel in an SE(T) specimen
    Link, Richard E.
    FATIGUE & FRACTURE MECHANICS, 35TH VOLUME, 2007, 35 : 485 - 510
  • [44] ON THE FAILURE MODE OF RESISTANCE SPOT WELDED HSLA 420 STEEL
    Pouranvari, M.
    ARCHIVES OF METALLURGY AND MATERIALS, 2013, 58 (01) : 67 - 72
  • [45] Fracture location transition in constant load tests of a NiCrMoV steel welded joint
    Weng, Shuo
    Huang, Yuhui
    Xuan, Fuzhen
    Zheng, Songlin
    MATERIALS & DESIGN, 2019, 181
  • [46] Fracture toughness of the materials in welded joint of X80 pipeline steel
    Yang, Yonghe
    Shi, Lei
    Xu, Zhen
    Lu, Hongsheng
    Chen, Xu
    Wang, Xin
    ENGINEERING FRACTURE MECHANICS, 2015, 148 : 337 - 349
  • [47] Effects of hydrogen and specimen thickness on fracture toughness of ferritic steel welded joint
    Li, Xiaogang
    Nie, Junfeng
    Wang, Xin
    Zhang, Haiquan
    INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2024, 82 : 11 - 24
  • [48] A STUDY OF PROCESS OF FRACTURE IN VARIOUS ZONES OF A WELDED JOINT IN LOW ALLOY STEEL
    NAVROTSK.IV
    SAVCHENK.VA
    MAKUKHIN, SI
    WELDING PRODUCTION, 1968, 15 (07): : 8 - &
  • [49] BRITTLE FRACTURE BEHAVIOR OF 9% Ni STEEL AND ITS WELDED JOINT.
    Arimochi, Kazushige
    Ohmori, Yasuya
    Kawaguchi, Yoshiaki
    Sumitomo Metals, 1982, 34 (02): : 1 - 18
  • [50] Research on fracture of steel structure welded joint based on micro-mechanism
    Qu, Xiushu
    Qin, Chenghao
    Sun, Guojun
    Xie, Yannan
    STRUCTURES, 2022, 43 : 434 - 448
12345