Stress corrosion cracking behavior and mechanism of 2205 duplex stainless steel under applied polarization potentials

被引：0
|
作者：
Pan, Yue [1 ,2 ]
Sun, Baozhuang [1 ]
Chen, Hetian [3 ]
Liu, Zhiyong [1 ]
Dai, Wenhe [4 ]
Yang, Xiaojia [1 ]
Yang, Weiting [2 ]
Deng, Yida [2 ]
Li, Xiaogang [1 ]
机构：
[1] National Materials Corrosion and Protection Scientific Data Center, Key Laboratory for Corrosion and Protection (MOE), University of Science and Technology Beijing, Beijing,100083, China
[2] Key Laboratory of Pico Electron Microscopy of Hainan Province, School of Materials Science and Engineering, Hainan University, Haikou,570228, China
[3] School of Materials Science and Engineering, University of New South Wales (UNSW Sydney), Sydney,2052, Australia
[4] Hebei Special Equipment Supervision and Inspection Institute, Key Laboratory of Safety Evaluation of Steel Pipes and Fittings for State Market Regulation, Shijiazhuang,050061, China
来源：
Corrosion Science | 2024年 / 231卷
基金：
中国国家自然科学基金;
关键词：
Cathodic polarization - Electrochemical corrosion - Hydrogen - Hydrogen embrittlement - Residual stresses - Stainless steel - Steel corrosion - Stress corrosion cracking;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
In this work, a non-steady electrochemical model for assessing stress corrosion cracking (SCC) of 2205 duplex stainless steel (DSS) under applied polarization potentials was proposed, and the SCC mechanism was revealed. With the negative shift of potentials, hydrogen enhances SCC susceptibility by deteriorating passive film, inhibiting repassivation and causing serious damage. In particular, at −850 mV (vs. SCE), the synergetic effect of anodic dissolution (AD) and hydrogen embrittlement (HE) causes severe pitting and SCC. The negative shift of applied potentials changes the preferential pit/SCC initiation site due to high hydrogen concentration in austenite. © 2024
引用
收藏
相关论文
共 50 条
  • [21] Effect of elastic tensile stress on the pitting corrosion mechanism and passive film of 2205 duplex stainless steel
    Xiao, Ying
    Lin, Bing
    Tang, Junlei
    Zheng, Hongpeng
    Wang, Yingying
    Zhang, Hailong
    Kuang, Yun
    Sun, Xiaoming
    ELECTROCHIMICA ACTA, 2024, 477
  • [22] Effect of Tensile Stress on Critical Pitting Temperature and Pitting Corrosion Behavior of 2205 Duplex Stainless Steel
    Hou Y.
    Cheng C.
    Zhao J.
    Feng X.
    Li R.
    Min X.
    Cailiao Daobao/Materials Review, 2019, 33 (03): : 1022 - 1026
  • [23] Electrochemical Corrosion Behavior of 2205 Duplex Stainless Steel Welds in Chloride Solutions
    Yan, HaiTao
    Xin, SenSen
    Yang, Yong
    Yang, Sai
    Li, MouCheng
    INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2019, 14 (02): : 1423 - 1433
  • [24] Effects of chitosan inhibitor on the electrochemical corrosion behavior of 2205 duplex stainless steel
    Se-fei Yang
    Ying Wen
    Pan Yi
    Kui Xiao
    Chao-fang Dong
    International Journal of Minerals Metallurgy and Materials, 2017, 24 (11) : 1260 - 1266
  • [25] Effects of chitosan inhibitor on the electrochemical corrosion behavior of 2205 duplex stainless steel
    Yang, Se-fei
    Wen, Ying
    Yi, Pan
    Xiao, Kui
    Dong, Chao-fang
    INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS, 2017, 24 (11) : 1260 - 1266
  • [26] Effects of chitosan inhibitor on the electrochemical corrosion behavior of 2205 duplex stainless steel
    Se-fei Yang
    Ying Wen
    Pan Yi
    Kui Xiao
    Chao-fang Dong
    International Journal of Minerals, Metallurgy, and Materials, 2017, 24 : 1260 - 1266
  • [27] Effects of hydrostatic pressure and pH on the corrosion behavior of 2205 duplex stainless steel
    Kan, Bo
    Wu, Weijie
    Yang, Zixuan
    Zhang, Xuewei
    Li, Jinxu
    JOURNAL OF ELECTROANALYTICAL CHEMISTRY, 2021, 886 (886)
  • [28] The metastable pitting corrosion of 2205 duplex stainless steel under bending deformation
    Hou, Yan
    Zhao, Jie
    Cheng, Cong-Qian
    Zhang, Lei
    Li, Jian
    Liu, Bao-Jun
    Cao, Tie-Shan
    JOURNAL OF ALLOYS AND COMPOUNDS, 2020, 830 (830)
  • [29] Electrochemical corrosion behavior of 2205 duplex stainless steel in hot concentrated seawater under vacuum conditions
    Yang, Yong
    Zeng, Hongtao
    Xin, Sensen
    Hou, Xueling
    Li, Moucheng
    CORROSION SCIENCE, 2020, 165
  • [30] Quantitative fractography of 2205 duplex stainless steel after a sulfide stress cracking test
    Klyk-Spyra, Katarzyna
    Sozanska, Maria
    MATERIALS CHARACTERIZATION, 2006, 56 (4-5) : 384 - 388
12345