High Temperature Mechanical Behavior of NbCr2/Nb Alloy

被引：0
|
作者：
Deng, Liping [1 ,2 ]
Lu, Shiqiang [1 ,2 ]
Tang, Binbing [3 ]
Lei, Zhili [2 ]
Gao, Jun [2 ]
机构：
[1] Nanjing University of Aeronautics and Astronautics, Nanjing,210016, China
[2] School of Aeronautical Manufacturing Engineering, Nanchang Hangkong University, Nanchang,330063, China
[3] Nanchang University, Nanchang,330031, China
来源：
Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering | 2019年 / 48卷 / 05期
关键词：
Compression testing - Deformation - Chromium alloys - Mechanical alloying - Hot pressing - Stacking faults - Strain rate - Niobium alloys - High resolution transmission electron microscopy;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
NbCr2/Nb alloy with the composition of Nb-22.5at%Cr was prepared by mechanical alloying and hot pressing process. Then compression tests were carried out under the condition of 800~1200℃ and 0.001~0.1 s-1. High temperature mechanical behavior and deformation mechanisms of the alloy were investigated by conventional transmission electron microscopy. The results show that the peak strength of the NbCr2/Nb alloy decreases with the increase of deformation temperature and the decrease of strain rate. The main deformation mechanism of Nb matrix is the slip of dislocation. While, the deformation mechanism of the Laves phase NbCr2 is through stacking fault/twins and partial dislocation. © 2019, Science Press. All right reserved.
引用
收藏
页码：1534 / 1538
相关论文
共 50 条
  • [41] Development of suicide coatings over Nb-NbCr2 alloy and their oxidation behavior at 1250 °C
    Qiao, Yanqiang
    Li, Maoyuan
    Guo, Xiping
    SURFACE & COATINGS TECHNOLOGY, 2014, 258 : 921 - 930
  • [42] Influence of grain size on the oxidation behavior of NbCr2 alloys at 950-1200 °C
    Zheng, H. Z.
    Lu, S. Q.
    Huang, Y.
    CORROSION SCIENCE, 2009, 51 (02) : 434 - 438
  • [43] THERMODYNAMIC ANALYSIS OF NANOCRYSTALLINE AND AMORPHOUS NbCr2 INTERMETALLIC PRODUCED BY MECHANICAL ALLOYING FOLLOWED BY HOT PRESSING
    Nie, Xiao-wu
    Lu, Shiqiang
    Wang, Kelu
    METAL SCIENCE AND HEAT TREATMENT, 2009, 51 (11-12) : 563 - 566
  • [44] Comments on "The absence of a stable hexagonal Laves phase modification (NbCr2) in the Nb-Cr system" Reply
    Nie, Xiao-wu
    SCRIPTA MATERIALIA, 2011, 64 (10) : 990 - 993
  • [45] Microstructure and strength of NbCr2/Cr in-situ composites
    Aoyama, N
    Hanada, S
    MATERIALS TRANSACTIONS JIM, 1997, 38 (02): : 155 - 162
  • [46] Phase transformations of NbCr2 intermetallics produced by mechanical alloying followed by hot-pressing consolidation
    Nie, X. W.
    Lu, S. Q.
    Wang, K. L.
    MATERIALS CHARACTERIZATION, 2008, 59 (06) : 816 - 819
  • [47] Laves相NbCr2/Nb两相合金热变形工艺参数优化
    江丰建聪
    鲁世强
    王克鲁
    邓莉萍
    肖璇
    塑性工程学报, 2023, 30 (02) : 141 - 151
  • [48] Microstructures and mechanical properties of NbCr2 and ZrCr2 Laves phase alloys prepared by powder metallurgy
    Ohta, T
    Nakagawa, Y
    Kaneno, Y
    Inoue, H
    Takasugi, IT
    Kim, WY
    JOURNAL OF MATERIALS SCIENCE, 2003, 38 (04) : 657 - 665
  • [49] Point defects in binary NbCr2 Laves-phase alloys
    Univ of Tennessee, Knoxville, United States
    Scripta Mater, 7 (833-838):
  • [50] Laves相NbCr2合金的研究进展
    马燕青
    鲁世强
    胡春文
    李鑫
    肖璇
    南昌航空工业学院学报(自然科学版), 2004, (04) : 28 - 31
12345