Effect of hydrogen on the pitting corrosion behavior of Incoloy 825

PurposeIn this paper, the authors aim to study the effect of hydrogen on the pitting corrosion behavior of Incoloy 825, a commonly used material for heat exchanger tubes in hydrogenated heat exchangers.Design/methodology/approachThe pitting initiation and propagation behaviors were investigated by electrochemical and chemical immersion experiments and observed and analyzed by scanning electron microscope and energy dispersive spectrometer methods.FindingsThe results show that hydrogen significantly affects the electrochemical behavior of Incoloy 825; the self-corrosion potential decreased from -197 mV before hydrogen charging to -263 mV, -270 mV and -657 mV after hydrogen charging, and the corrosion current density increased from 0.049 mu A/cm2 before hydrogen charging to 2.490 mu A/cm2, 2.560 mu A/cm2 and 2.780 mu A/cm2 after hydrogen charging. The pitting susceptibility of the material increases.Originality/valueHydrogen is enriched on the precipitate, and the pitting corrosion also initiates at that location. The synergistic effect of hydrogen and precipitate destroys the passive film on the metal surface and promotes pitting initiation.