High-temperature oxidation resistance of Si-coated C/SiC composites

被引：0
|
作者：
Jie Xiao [1 ]
HuaYue Zhang [1 ]
ShengKai Gong [1 ,2 ]
HuiBin Xu [1 ,2 ]
HongBo Guo [1 ,2 ]
机构：
[1] School of Materials Science and Engineering,Beihang University
[2] Key Laboratory of High-Temperature Structure Materials and Protective Coatings (Ministry of Industry and Information Technology),Beihang
来源：
RareMetals | 2024年 / 43卷 / 09期
关键词：
D O I：
暂无
中图分类号：
TB332 [非金属复合材料];
学科分类号：
摘要：
In this paper, Si coatings were sprayed onto C/Si C composite substrates by atmospheric plasma spraying(APS). The high-temperature oxidation behavior of the substrate and coating at temperatures of 1100 and 1300 °C was also studied. The C/Si C ceramic matrix composite will be damaged seriously and even failed due to the oxidation of carbon fibers in matrix. The Si coating effectively improved the oxidation resistance of the C/Si C substrate in the high-temperature oxidation test. The effect of the thickness of the Si coatings on the oxidation resistance was investigated. The 150-μm coating is proved to enable the substrate to have the lowest oxidation weight loss and the best oxidation resistance after static oxidation for 5 h.
引用
收藏
页码：4566 / 4572
页数：7
相关论文
共 50 条
  • [41] Technological advances in high-temperature protection of C/C-SiC composites
    Zhou F.
    Cao Y.
    Liu R.
    Wang Y.
    Zuo L.
    Cao, Yingbin (caoyingbin@nudt.edu.cn), 2016, Cailiao Daobaoshe/ Materials Review (30): : 68 - 74
  • [42] SiC fibers with different diameters exhibiting excellent high-temperature resistance and oxidation resistance
    Kang, Weifeng
    Chen, Jiahui
    Zhang, Yu
    Zhang, Qingyu
    Chen, Tianxie
    Gou, Yanzi
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2023, 23 : 1559 - 1569
  • [43] Formation process of Si-coated C60
    Tanaka, H
    Osawa, S
    Onoe, J
    Takeuchi, K
    JOURNAL OF PHYSICAL CHEMISTRY B, 1999, 103 (29): : 5939 - 5942
  • [44] High temperature oxidation behaviour of mullite coated C/C composites in air
    Fritze, H
    Lenk, A
    Witke, T
    Weber, S
    Scherrer, S
    Weiss, R
    Schultrich, B
    Borchardt, G
    HIGH TEMPERATURE CORROSION AND PROTECTION OF MATERIALS 4, PTS 1 AND 2, 1997, 251-2 : 909 - 915
  • [45] High-temperature flexural properties of SiBC modified C/SiC composites
    Cao, Xiaoyu
    Yin, Xiaowei
    Fan, Xiaomeng
    Zhao, Ke
    Luo, Huijuan
    Cheng, Laifei
    Zhang, Litong
    CERAMICS INTERNATIONAL, 2014, 40 (04) : 6185 - 6190
  • [46] Oxidation behavior of C/SiC-SiBCN composites at high temperature
    Luan, Xin'gang
    Wang, Lei
    Zou, Yun
    Zhang, Qiqi
    Riedel, Ralf
    Cheng, Laifei
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2019, 39 (10) : 3003 - 3012
  • [47] Formation process of Si-coated C60
    Tanaka, Hideki
    Osawa, Shuichi
    Onoe, Jun
    Takeuchi, Kazuo
    Journal of Physical Chemistry B, 103 (29): : 5939 - 5942
  • [48] A Si-Mo oxidation protective coating for C/SiC coated carbon/carbon composites
    Zhang Yu-Lei
    Li He-Jun
    Fu Qian-Gang
    Li Ke-Zhi
    Hou Dang-She
    Fei Jie
    CARBON, 2007, 45 (05) : 1130 - 1133
  • [49] Oxidation resistance and mechanical properties of HfC nanowire-toughened ultra-high temperature ceramic coating for SiC-coated C/C composites
    Ren, Jincui
    Zhang, Yulei
    Hu, Heng
    Fei, Tian
    Li, Hejun
    APPLIED SURFACE SCIENCE, 2016, 360 : 970 - 978
  • [50] High-temperature oxidation resistance of Ta-Si-N films with a high Si content
    Zeman, P
    Musil, J
    Daniel, R
    SURFACE & COATINGS TECHNOLOGY, 2006, 200 (12-13): : 4091 - 4096
12345