High-temperature oxidation resistance of Si-coated C/SiC composites

被引：0
|
作者：
Jie Xiao [1 ]
HuaYue Zhang [1 ]
ShengKai Gong [1 ,2 ]
HuiBin Xu [1 ,2 ]
HongBo Guo [1 ,2 ]
机构：
[1] School of Materials Science and Engineering,Beihang University
[2] Key Laboratory of High-Temperature Structure Materials and Protective Coatings (Ministry of Industry and Information Technology),Beihang
来源：
RareMetals | 2024年 / 43卷 / 09期
关键词：
D O I：
暂无
中图分类号：
TB332 [非金属复合材料];
学科分类号：
摘要：
In this paper, Si coatings were sprayed onto C/Si C composite substrates by atmospheric plasma spraying(APS). The high-temperature oxidation behavior of the substrate and coating at temperatures of 1100 and 1300 °C was also studied. The C/Si C ceramic matrix composite will be damaged seriously and even failed due to the oxidation of carbon fibers in matrix. The Si coating effectively improved the oxidation resistance of the C/Si C substrate in the high-temperature oxidation test. The effect of the thickness of the Si coatings on the oxidation resistance was investigated. The 150-μm coating is proved to enable the substrate to have the lowest oxidation weight loss and the best oxidation resistance after static oxidation for 5 h.
引用
收藏
页码：4566 / 4572
页数：7
相关论文
共 50 条
  • [1] High-temperature oxidation resistance of Si-coated C/SiC composites
    Xiao, Jie
    Zhang, Hua-Yue
    Gong, Sheng-Kai
    Xu, Hui-Bin
    Guo, Hong-Bo
    RARE METALS, 2024, 43 (09) : 4566 - 4572
  • [2] High temperature oxidation behavior of SiC-coated C/C composites
    Aoki, T
    Hatta, H
    Kogo, Y
    Fukuda, H
    Goto, Y
    Yarii, T
    JOURNAL OF THE JAPAN INSTITUTE OF METALS, 1998, 62 (04) : 404 - 412
  • [3] High temperature oxidation behavior of SiC-coated C/C composites
    Aoki, Takuya
    Hatta, Hiroshi
    Kogo, Yasuo
    Fukuda, Hiroshi
    Goto, Yasuhiro
    Yarii, Toshio
    Nippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals, 1998, 62 (04): : 404 - 412
  • [4] Oxidation behavior and high-temperature flexural property of CVD-SiC-coated PIP-C/SiC composites
    Wen Jin
    Zhou Si
    Yi Lu
    Sun Bei-zhi
    Wang Yi
    Li Guang-de
    Xing Zhong-fang
    Cao Jie
    He Heng-ping
    Xiang Yang
    CERAMICS INTERNATIONAL, 2018, 44 (14) : 16583 - 16588
  • [5] Oxidation protection of C/SiC coated carbon/carbon composites with Si-Mo coating at high temperature
    Zhang, Yu-Lei
    Li, He-Jun
    Yao, Xi-Yuan
    Li, Ke-Zhi
    Qiang, Xin-Fa
    CORROSION SCIENCE, 2011, 53 (06) : 2075 - 2079
  • [6] Effect of residual silicon on the oxidation resistance of bilayer Yb2Si2O7/SiC coated C/SiC composites at high temperature
    Chen, Pengju
    Xiao, Peng
    Li, Zhuan
    Li, Jinwei
    Pu, Dongmei
    Deng, Pingyi
    Li, Yang
    CORROSION SCIENCE, 2020, 170
  • [7] High-temperature oxidation resistance behavior and mechanism of HfSiO 4-modified C/SiC composites
    Qiu, Jintao
    Yang, Huiyong
    Huang, Juntong
    Wang, Lianyi
    Luo, Ruiying
    Chen, Zhi
    Li, Wei
    Deng, Chengmou
    Li, Wenpeng
    Zhang, Jinxuan
    Tao, Zejian
    Zhong, Shujun
    Teng, Wenhao
    CERAMICS INTERNATIONAL, 2024, 50 (12) : 21755 - 21766
  • [8] Influence of preparation temperature on the oxidation resistance and mechanical properties of C/SiC coated C/C composites
    Zhang, Yu-Lei
    Hu, Zhi-Xiong
    Ren, Jin-Cui
    Li, He-Jun
    Yang, Bo-Xing
    Zhang, Lei-Lei
    CORROSION SCIENCE, 2014, 86 : 337 - 342
  • [9] Oxidation resistant Si-Mo-Al coating for C/SiC coated carbon/carbon composites at high temperature
    Zhang, Y. -L.
    Li, H. -J.
    Yao, X. -Y.
    Li, K. -Z.
    Qiang, X. -F.
    SURFACE ENGINEERING, 2012, 28 (04) : 257 - 260
  • [10] Oxidation resistance behavior of SiC nanowires/Si layer on the C/SiC composites
    Wang, Bo
    Li, Jiayan
    Zhang, Fan
    He, Ping
    Shi, Wei
    Tan, Yi
    MATERIALS CHARACTERIZATION, 2023, 197
12345