Microstructure and Nano-Hardness of 10 MeV Cl-Ion Irradiated T91 Steel

被引：0
|
作者：
胡菁 [1 ,2 ]
王先平 [1 ]
高云霞 [1 ]
庄重 [1 ]
张涛 [1 ]
方前锋 [1 ]
刘长松 [1 ]
机构：
[1] Key Laboratory of Materials Physics,Institute of Solid State Physics,Chinese Academy of Sciences
[2] School of Physics and Electronic Information,Huaibei Normal
来源：
Plasma Science and Technology | 2015年 / 12期
关键词：
D O I：
暂无
中图分类号：
TG142.1 [钢的组织与性能];
学科分类号：
摘要：
Hardening and elemental segregation of T91 martenstic steel irradiated by 10 MeV Cl ions to doses from 0.06 dpa to 0.83 dpa were investigated with the nanoindentation technique and transmission electron microscopy（TEM）.The results demonstrated that the irradiation hardening was closely related with irradiation dose.By increasing the dose,the hardness increased rapidly at first from the initial value of 3.15 GPa before irradiation,and then tended to saturate at a value of 3.58 GPa at the highest dose of 0.83 dpa.Combined with TEM observation,the mechanism of hardening was preliminary attributed to the formation of M（Fe,Cr）23C6 carbides induced by the high energy Cl-ion irradiation.
引用
收藏
页码：1088 / 1091
页数：4
相关论文
共 50 条
  • [41] Effect of Surface Mechanical Attrition Treatment on Microstructure and Oxidation Behavior in T91 Steel at High Temperature
    Xia, Zhi-xin
    Zhang, Chi
    Liu, Wen-bo
    Yang, Zhi-gang
    ISIJ INTERNATIONAL, 2014, 54 (08) : 1935 - 1942
  • [42] Hardening of high-energy self-ion irradiated FeCrAl ODS alloys evaluated by micro- and nano-hardness tests
    Han, Xuxiao
    Zhang, Chonghong
    Yang, Yitao
    Niu, Mengke
    Wang, Tieshan
    Kimura, Akihiko
    INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 2021, 194
  • [43] Microstructure and fracture morphology in the welding zone of T91 heat-resisting steel used in power station
    Li, YJ
    Zhou, B
    Feng, T
    Ren, JW
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2002, 18 (05) : 427 - 430
  • [44] Microstructure and Fracture Morphology in the Welding Zone of T91 Heat-resisting Steel Used in Power Station
    YajiangLI
    BingZHOU
    TaoFENG
    JiangweiREN
    Journal of Materials Science & Technology, 2002, (05) : 427 - 430
  • [45] SANS and TEM of ferritic-martensitic steel T91 irradiated in FFTF up to 184 dpa at 413 °C
    Van den Bosch, J.
    Anderoglu, O.
    Dickerson, R.
    Hartl, M.
    Dickerson, P.
    Aguiar, J. A.
    Hosemann, P.
    Toloczko, M. B.
    Maloy, S. A.
    JOURNAL OF NUCLEAR MATERIALS, 2013, 440 (1-3) : 91 - 97
  • [46] Micro-hardness measurement and micro-structure characterization of T91 weld metal irradiated in SINQ Target-3
    Jia, X
    Dai, Y
    JOURNAL OF NUCLEAR MATERIALS, 2005, 343 (1-3) : 212 - 218
  • [47] EFFECT OF SEVERE PLASTIC DEFORMATION AT HIGH TEMPERATURE ON THE MICROSTRUCTURE AND MECHANICAL PROPERTIES OF FERRITIC-MARTENSITIC STEEL T91
    Rostova, H. Yu.
    Kolodiy, I. V.
    Vasilenko, R. L.
    Kalchenko, O. S.
    Tikhonovsky, M. A.
    Velikodnyi, O. M.
    Tolstolutska, G. D.
    Okovit, V. S.
    PROBLEMS OF ATOMIC SCIENCE AND TECHNOLOGY, 2024, (04): : 54 - 63
  • [48] Microstructure and fracture morphology in the welding zone of T91 heat-resistant steel used in power station.
    Li, Yajiang
    Zhou, Bing
    Feng, Tao
    Ren, Jiangwei
    Journal of Materials Science and Technology, 2002, 18 (05): : 427 - 430
  • [49] Microstructure and property of long-time run T91/G102 dissimilar steel welded joint
    State Key Laboratory for Advanced Metals and Materials, Beijing University of Science and Technology, Beijing 100083, China
    不详
    不详
    Hanjie Xuebao, 2007, 3 (17-20):
  • [50] Early-stage microstructural evolution and phase stability in neutron-irradiated ferritic-martensitic steel T91
    Yan, Huan
    Liu, Xiang
    He, Lingfeng
    Stubbins, James
    JOURNAL OF NUCLEAR MATERIALS, 2021, 557
12345