DETERMINATION OF INDIVIDUAL CORROSION-FATIGUE RESISTANCE CHARACTERISTICS

被引:0
|
作者
OLEINIK, NV
KONOPLEV, AV
机构
来源
INDUSTRIAL LABORATORY | 1994年 / 60卷 / 12期
关键词
D O I
暂无
中图分类号
TH7 [仪器、仪表];
学科分类号
0804 ; 080401 ; 081102 ;
摘要
A method for plotting the individual corrosion fatigue curve of a test object (a material specimen or a machine part) is proposed. The left-hand portion of the curve is described by an exponential equation, and the right-hand portion, by a fractional linear function. The curve thus plotted provides a more rigorous description of the behavior of steel specimens in the long-term endurance range compared to a curve that obeys only a single exponential equation.
引用
收藏
页码:733 / 735
页数:3
相关论文
共 50 条
  • [21] NEW APPROACHES IN CORROSION-FATIGUE TESTING
    KHOBAIB, M
    LYNCH, CT
    JOURNAL OF METALS, 1980, 32 (12): : 8 - 8
  • [22] Corrosion-Fatigue Crack-Growth Resistance of Steel of the Frame of a Sprayer Boom
    А. М. Syrotyuk
    А. V. Babii
    R. А. Barna
    R. L. Leshchak
    P. О. Marushchak
    Materials Science, 2021, 56 : 466 - 471
  • [23] MECHANICAL SITUATION AT THE TIP OF A CORROSION-FATIGUE CRACK AND THE CYCLIC CRACK RESISTANCE OF STEELS
    NIKIFORCHIN, GN
    SOVIET MATERIALS SCIENCE, 1988, 24 (02): : 105 - 114
  • [24] METHODS FOR COMPARISON OF RESULTS OF FATIGUE AND CORROSION-FATIGUE TESTS
    KARLASHO.AV
    TOKAREV, VP
    BATOV, AP
    SAZONOV, VV
    ZAVODSKAYA LABORATORIYA, 1974, 40 (10): : 1250 - 1252
  • [25] Changes in the electrochemical characteristics of corrosion-resistant steels at the beginning of the process of corrosion-fatigue damage
    Khoma, MS
    Pokhmurs'kyi, VI
    MATERIALS SCIENCE, 2003, 39 (01) : 1 - 7
  • [26] Corrosion-Fatigue Crack-Growth Resistance of Steel of the Frame of a Sprayer Boom
    Syrotyuk, A. M.
    Babii, A. V.
    Barna, R. A.
    Leshchak, R. L.
    Marushchak, P. O.
    MATERIALS SCIENCE, 2021, 56 (04) : 466 - 471
  • [27] Changes in the Electrochemical Characteristics of Corrosion-Resistant Steels at the Beginning of the Process of Corrosion-Fatigue Damage
    M. S. Khoma
    V. I. Pokhmurs'kyi
    Materials Science, 2003, 39 : 1 - 7
  • [28] Corrosion and corrosion-fatigue of AZ31 Magnesium weldments
    C. E. Cross
    P. Xu
    N. Winzer
    S. Bender
    D. Eliezer
    Welding in the World, 2011, 55 : 40 - 47
  • [29] USE OF ACOUSTIC-EMISSION TO MONITOR CORROSION AND CORROSION-FATIGUE
    BASSIM, MN
    CIM BULLETIN, 1988, 81 (914): : 86 - 86
  • [30] A peridynamic model for corrosion-fatigue failure behaviour
    Wu, Haoqi
    Qi, Hongyu
    Li, Shaolin
    Zhao, Gaole
    Yang, Xiaoguang
    Shi, Duoqi
    THEORETICAL AND APPLIED FRACTURE MECHANICS, 2023, 127