OXYGEN NONSTOICHIOMETRY OF 2223-PHASE BI-PB-SR-CA-CU-O SYSTEM SUPERCONDUCTING OXIDE

被引：62
|
作者：
IDEMOTO, Y
ICHIKAWA, S
FUEKI, K
机构：
[1] Department of Industrial Chemistry, Faculty of Science and Technology, Science University of Tokyo, Noda-shi, Chiba, 278
来源：
PHYSICA C | 1991年 / 181卷 / 1-3期
关键词：
D O I：
10.1016/0921-4534(91)90351-X
中图分类号：
O59 [应用物理学];
学科分类号：
摘要：
The oxygen nonstoichiometry of Bi1.74Pb0.27Sr1.86Ca2.09Oy (2223 phase) was determined as a function of temperature and oxygen partial pressure under the condition that Ca2PbO4 was not formed. It was also found that PbO evaporated from the 2223 phase about 700-degrees-C in a low oxygen pressure range. Below about 700-degrees-C, the dependences of oxygen content on both temperature and oxygen partial pressure were weak, whereas they were strong above 700-degrees-C. The effect of PbO content on properties of the 2223 phase was studied by allowing PbO to evaporate under 500-degrees-C and 800-degrees-C in oxygen of 0.01 atm for different annealing periods. It was found that the critical temperature and the valences of copper and bismuth remained constant in spite of a loss of PbO.
引用
收藏
页码：171 / 178
页数：8
相关论文
共 50 条
  • [21] SUPERCONDUCTING GLASS-CERAMICS IN BI-PB-SR-CA-CU-O SYSTEM
    BAHADUR, D
    BANERJEE, A
    DAS, A
    GUPTA, KP
    MITRA, A
    TEWARI, M
    MAJUMDAR, AK
    MATERIALS RESEARCH BULLETIN, 1989, 24 (11) : 1405 - 1412
  • [22] EFFECT OF CA2CUO3 ON THE FORMATION OF (2223)-PHASE IN THE BI-PB-SR-CA-CU-O SYSTEM
    KISHORE, KN
    MURALIDHAR, M
    BABU, VH
    MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY, 1992, 14 (04): : 401 - 407
  • [23] Formation process of 2223 phase in Bi-Pb-Sr-Ca-Cu-O system via calcining at 1073 K
    Shimono, I
    Kijima, N
    Nagata, S
    Konishi, H
    Hamaguchi, Y
    JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, 1996, 104 (02) : 101 - 108
  • [24] GROWTH OF THE 2223-PHASE IN BI-SR-CA-CU OXIDE-FILMS UNDER A CONTROLLED PB POTENTIAL
    HAYAKAWA, H
    KAISE, M
    NAKAMURA, K
    OGAWA, K
    JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS & EXPRESS LETTERS, 1989, 28 (06): : L967 - L969
  • [25] COMPOSITION DEPENDENCE ON THE SUPERCONDUCTING PROPERTIES OF BI-PB-SR-CA-CU-O
    ENDO, U
    KOYAMA, S
    KAWAI, T
    JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS, 1989, 28 (02): : L190 - L192
  • [26] Crystallization kinetics of superconducting precursor glasses in the Bi-Pb-Sr-Ca-Cu-O system
    Urano, T
    Khaled, J
    Komatsu, T
    Chaudhuri, BK
    THERMOCHIMICA ACTA, 1999, 325 (02) : 133 - 142
  • [27] EFFECT OF SUPERCOOLING ON THE GROWTH-KINETICS OF THE 2223 PHASE IN BI-PB-SR-CA-CU-O SUPERCONDUCTING GLASS-CERAMICS
    SHAN, CH
    RISBUD, SH
    SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 1993, 6 (10): : 736 - 742
  • [28] SUPERCONDUCTING PROPERTIES OF AU/BI-PB-SR-CA-CU-O COMPOSITES
    LIU, HK
    DOU, SX
    SONG, KH
    SORRELL, CC
    SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 1990, 3 (04): : 210 - 212
  • [29] INFLUENCE OF INTERMEDIATE PRESSING ON SUPERCONDUCTING CHARACTERISTICS IN BI-PB-SR-CA-CU-O SYSTEM
    ITO, A
    MATSUDA, M
    IWAI, Y
    ISHII, M
    TAKATA, M
    YAMASHITA, T
    KOINUMA, H
    JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS, 1989, 28 (03): : L380 - L381
  • [30] SUPERCONDUCTING CHARACTERISTICS AND MICROSTRUCTURE OF BI-PB-SR-CA-CU-O CERAMICS
    KIKUCHI, A
    MATSUDA, M
    TAKATA, M
    ISHII, M
    YAMASHITA, T
    KOINUMA, H
    JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS & EXPRESS LETTERS, 1988, 27 (12): : L2300 - L2303
12345