OXYGEN NONSTOICHIOMETRY OF 2223-PHASE BI-PB-SR-CA-CU-O SYSTEM SUPERCONDUCTING OXIDE

被引：62
|
作者：
IDEMOTO, Y
ICHIKAWA, S
FUEKI, K
机构：
[1] Department of Industrial Chemistry, Faculty of Science and Technology, Science University of Tokyo, Noda-shi, Chiba, 278
来源：
PHYSICA C | 1991年 / 181卷 / 1-3期
关键词：
D O I：
10.1016/0921-4534(91)90351-X
中图分类号：
O59 [应用物理学];
学科分类号：
摘要：
The oxygen nonstoichiometry of Bi1.74Pb0.27Sr1.86Ca2.09Oy (2223 phase) was determined as a function of temperature and oxygen partial pressure under the condition that Ca2PbO4 was not formed. It was also found that PbO evaporated from the 2223 phase about 700-degrees-C in a low oxygen pressure range. Below about 700-degrees-C, the dependences of oxygen content on both temperature and oxygen partial pressure were weak, whereas they were strong above 700-degrees-C. The effect of PbO content on properties of the 2223 phase was studied by allowing PbO to evaporate under 500-degrees-C and 800-degrees-C in oxygen of 0.01 atm for different annealing periods. It was found that the critical temperature and the valences of copper and bismuth remained constant in spite of a loss of PbO.
引用
收藏
页码：171 / 178
页数：8
相关论文
共 50 条
  • [1] EFFECTS OF SB-INCORPORATION ON THE 2223 PHASE IN THE SUPERCONDUCTING BI-PB-SR-CA-CU-O SYSTEM
    KIM, SH
    LEE, DH
    PARK, JS
    CHO, SK
    LEE, SH
    KIM, KH
    BULLETIN OF THE KOREAN CHEMICAL SOCIETY, 1994, 15 (02) : 115 - 118
  • [2] Synthesis and phase relations of the 110 K superconducting 2223 phase in the Bi-Pb-Sr-Ca-Cu-O system
    Bernik, S
    SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 1997, 10 (09): : 671 - 677
  • [3] BI,PB(2212) AND BI(2223) FORMATION IN THE BI-PB-SR-CA-CU-O SYSTEM
    JEREMIE, A
    ALAMIYADRI, K
    GRIVEL, JC
    FLUKIGER, R
    SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 1993, 6 (10): : 730 - 735
  • [4] PREPARATION AND PROPERTIES OF PHASE-2223 IN THE BI-PB-SR-CA-CU-O SYSTEM
    DROZDOVA, NM
    DUBENKO, IS
    EVDOKIMOV, AA
    LAPTEV, AG
    SMIRNOV, SA
    TITOV, YV
    ZHURNAL NEORGANICHESKOI KHIMII, 1991, 36 (06): : 1368 - 1371
  • [5] HIGH-TEMPERATURE CONDUCTIVITY OF 2223 PHASE OF BI-PB-SR-CA-CU-O SUPERCONDUCTING OXIDES
    IDEMOTO, Y
    FUJIWARA, S
    FUEKI, K
    PHYSICA C, 1991, 179 (1-3): : 96 - 100
  • [6] GROWTH OF THE HIGH-TC PHASE IN THE BI-PB-SR-CA-CU-O SUPERCONDUCTING OXIDE SYSTEM
    HAYASHI, Y
    KOGURE, H
    GONDO, Y
    JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS & EXPRESS LETTERS, 1989, 28 (12): : L2182 - L2184
  • [7] ON THE FORMATION OF THE 2223-PHASE IN THE BI-PB-SR-CA-CU-O SYSTEM USING PB0.2SRCA(CO3)2.2 PRECURSORS
    PANDEY, D
    MAHESH, R
    SINGH, AK
    TIWARI, VS
    KAK, SK
    SOLID STATE COMMUNICATIONS, 1990, 76 (05) : 655 - 658
  • [8] CU VALENCE STATES IN SUPERCONDUCTING BI-PB-SR-CA-CU-O SYSTEM
    LIU, HK
    DOU, SX
    SONG, KH
    SORRELL, CC
    EASTERLING, KE
    JONES, WK
    JOURNAL OF SOLID STATE CHEMISTRY, 1990, 87 (02) : 289 - 297
  • [9] INDIUM DOPING IN THE BI-PB-SR-CA-CU-O SUPERCONDUCTING SYSTEM
    NKUM, RK
    PUNNETT, A
    UMMAT, PK
    DATARS, WR
    PHYSICA C, 1992, 194 (3-4): : 321 - 326
  • [10] SUBSTITUTION OF SN IN THE SUPERCONDUCTING BI-PB-SR-CA-CU-O SYSTEM
    NKUM, RK
    DATARS, WR
    PHYSICA C, 1992, 190 (04): : 465 - 470
12345