CORROSION FATIGUE BEHAVIOR OF 13CR MARTENSITIC STAINLESS-STEELS IN 3-PERCENT NACL SOLUTION WITH A SPECIAL REFERENCE TO THEIR INTERGRANULAR CORROSION SUSCEPTIBILITY

被引：1
|
作者：
OZAKI, T [1 ]
ISHIKAWA, Y [1 ]
MUKAI, Y [1 ]
机构：
[1] OSAKA UNIV,FAC ENGN,OSAKA,JAPAN
来源：
TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN | 1989年 / 75卷 / 03期
关键词：
D O I：
10.2355/tetsutohagane1955.75.3_523
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
引用
收藏
页码：523 / 528
页数：6
相关论文
共 50 条
  • [31] STRESS-CORROSION CRACKING IN HIGH-TEMPERATURE PURE WATER AND SELECTIVE CORROSION OF NICKEL-BEARING CR-13 MARTENSITIC STAINLESS-STEELS
    OZAKI, T
    ISHIKAWA, Y
    JOURNAL OF THE JAPAN INSTITUTE OF METALS, 1988, 52 (09) : 852 - 858
  • [32] THE EFFECTS OF STRAIN RATE ON THE CORROSION FATIGUE BEHAVIOR OF BCC FE-26CR-1MO STAINLESS-STEELS
    MAGNIN, T
    COUDREUSE, L
    MATERIALS SCIENCE AND ENGINEERING, 1985, 72 (02): : 125 - 134
  • [33] CORROSION-FATIGUE CRACK INITIATION BEHAVIOR OF DUPLEX STAINLESS-STEEL IN 0.9-PERCENT-NACL SOLUTION
    HIGO, Y
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1984, 70 (13): : 1438 - 1438
  • [34] EFFECTS OF NI ON STRESS-CORROSION SUSCEPTIBILITY OF HIGH-CR FERRITIC STAINLESS-STEELS IN HOT CL- SOLUTION
    KWON, HS
    JANG, SP
    CORROSION, 1993, 49 (10) : 802 - 808
  • [35] Effects of temperature on the corrosion behavior of 13Cr martensitic stainless steel during exposure to CO2 and Cl- environment
    Zhang, H
    Zhao, YL
    Jiang, ZD
    MATERIALS LETTERS, 2005, 59 (27) : 3370 - 3374
  • [36] The Growth Behavior and Mechanisms of Pitting Corrosion on Super 13Cr Martensitic Stainless Steel Surfaces at Different Diameter-to-Depth Ratios
    Yang, Zichen
    Dong, Hui
    Han, Yan
    Zhang, Yongjie
    Li, Pengyu
    Feng, Yukun
    COATINGS, 2024, 14 (04)
  • [37] Corrosion Behavior of Fe-based Amorphous Alloys and 13Cr Stainless Steels under Supercritical CO2 Environment
    Yao, Ying
    Yang, Baijun
    Zhang, Suode
    Qiu, Keqiang
    CHINA SURFACE ENGINEERING, 2023, 36 (01) : 85 - 94
  • [38] Effects of solution composition on corrosion behavior of 13 mass% Cr martensitic stainless steel in simulated oil and gas environments
    Sakairi, Masatoshi
    Mizukami, Hirotaka
    Hashizume, Shuji
    AIMS MATERIALS SCIENCE, 2019, 6 (02) : 288 - 300
  • [39] EFFECTS OF NICKEL AND NITROGEN ON THE STRESS-CORROSION CRACKING SUSCEPTIBILITY OF AUSTENITIC STAINLESS-STEELS IN H2SO4-NACL SOLUTION
    KAMIDE, H
    SUGAWARA, H
    JOURNAL OF THE JAPAN INSTITUTE OF METALS, 1979, 43 (08) : 721 - 727
  • [40] Stress corrosion cracking behavior and mechanism of super 13Cr stainless steel in simulated O2/CO2 containing 3.5 wt% NaCl solution
    Luo, Sheji
    Fu, Anqing
    Liu, Ming
    Xue, Yuna
    Lv, Naixin
    Han, Yan
    ENGINEERING FAILURE ANALYSIS, 2021, 130
12345