Characterization of PbS thin films obtained by chemical bath at low temperature using sodium citrate as complexing agent

The deposition of PbS thin films by the chemical bath deposition method using sodium citrate as non-toxic complexing agent is presented. As-deposited PbS films and those annealed at 200 and 300 degrees C in argon atmosphere were formed by tightly compact spherical particles homogeneously distributed along the substrates. The XRD analysis shows that all the films had a galena type cubic crystalline structure. The crystallite size of the as-deposited film was 17 nm which decreased to 14 nm when the film was annealed to 300 degrees C. Thermal treatments to the films produced a shift of the optical band gap from 1.34 to 1.49 eV. Furthermore, the asdeposited PbS films were photosensitive showing a conductivity of 10(-2) Omega(-1) cm(-1) under illumination. Such a conductivity increased to 10(-1) Omega(-1) cm(-1) with the thermal treatment at 200 degrees C. The evaluation of the PbS film using a CdS thin film partner as window in the solar cell configuration showed an open circuit voltage of 88 mV and a short current density of 3.5 mA/cm(2).