PREPARATION OF MONODISPERSED ZIRCONIA-ALUMINA AND YTTRIA-ALUMINA PARTICLES

被引：6

作者：

OGIHARA, T ^{[1
]}

WADA, K ^{[1
]}

YOSHIDA, T ^{[1
]}

YANAGAWA, T ^{[1
]}

OGATA, N ^{[1
]}

YOSHIDA, K ^{[1
]}

MATSUSHITA, N ^{[1
]}

机构：

[1] TAKEFU FINE CHEM CO LTD,TAKEFU,FUKUI 915,JAPAN

来源：

CERAMICS INTERNATIONAL | 1993年 / 19卷 / 03期

关键词：

D O I：

10.1016/0272-8842(93)90037-R

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Alkoxide route involving the use of an emulsion technique enabled monodispersed, spherical zirconia-alumina and yttria-alumina particles of submicrometer size to be formed. The effects of the concentration of reactants and their ratio, organic solvents, and HPC dispersant on particle size, size distribution, morphology, and aggregation were investigated. EDS analysis showed little particle compositional fluctuation. Unstabilized tetragonal zirconia was retained in an alumina matrix up to 15 mol% zirconium alkoxide content at 1400 degrees C. Yttrium aluminum garnet was formed in yttria-alumina powders calcined at 1000 degrees C. The calcination at 1000 degrees C also resulted in particles that retained their spherical morphology. The isoelectric point of zirconia-alumina and yttria-alumina particles occurred from pH 9 to 10.

引用

页码：159 / 168

页数：10

共 50 条

[21] Yttria-stabilized zirconia-alumina composite sintering temperature effect on thermal diffusivity
Dychton, Kamil
Drajewicz, Marcin
Pytel, Maciej
Rokicki, Pawe
Nowotnik, Andrzej
JOURNAL OF THERMAL ANALYSIS AND CALORIMETRY, 2016, 126 (01) : 1 - 7
[22] Preparation and evaluation of zirconia-alumina composites for high performance liquid chromatograpy
Wan, JD
Feng, YQ
Hu, YL
Da, SL
Wang, ZH
CHINESE JOURNAL OF ANALYTICAL CHEMISTRY, 2001, 29 (07) : 802 - 805
[23] Liquid-Liquid Phase Transition in Supercooled Yttria-Alumina
Barnes, Adrian C.
Skinner, Lawrie B.
Salmon, Philip S.
Bytchkov, Alexei
Pozdnyakova, Irina
Farmer, Thomas O.
Fischer, Henry E.
PHYSICAL REVIEW LETTERS, 2009, 103 (22)
[24] Zirconia-alumina: An alternative bearing for hip arthroplasty
Weber, WR
Rieger, W
Clausen, J
Schmotzer, H
BIOCERAMICS, 2000, 192-1 : 533 - 536
[25] Novel yttria-stabilised zirconia-alumina tetragonal phase obtained by co-precipitation
Santoyo-Salazar, J
Gonzalez, G
Ascencio, JA
Tartaj-Salvador, J
Chávez-Carvayar, JA
JOURNAL OF CRYSTAL GROWTH, 2006, 290 (01) : 307 - 312
[26] Formation of Pore Structure in Zirconia-Alumina Ceramics
Buyakov, Ales S.
Levkov, Ruslan V.
Buyakova, Svetlana P.
Kurovics, Emese
Gomze, Laszlo A.
Kulkov, Sergei N.
EPITOANYAG-JOURNAL OF SILICATE BASED AND COMPOSITE MATERIALS, 2018, 70 (01): : 27 - 31
[27] ZIRCONIA-ALUMINA PARTICULATE COMPOSITES BY INFILTRATION PROCESSING
RIOU, S
QUEYROUX, F
BOCH, P
CERAMICS INTERNATIONAL, 1995, 21 (05) : 339 - 343
[28] Synthesis and characterization of zirconia-alumina mixed oxides
Dumeignil, F
Blanchard, P
Payen, E
Grimblot, J
Poulet, O
HYDROTREATMENT AND HYDROCRACKING OF OIL FRACTIONS, 1997, 106 : 547 - 560
[29] COMBUSTION SYNTHESIS AND PROPERTIES OF ZIRCONIA-ALUMINA POWDERS
DHAS, NA
PATIL, KC
CERAMICS INTERNATIONAL, 1994, 20 (01) : 57 - 66
[30] Zirconia-alumina mixing in alumina-supported zirconia prepared by impregnation with solutions of zirconium acetylacetonate
Faro, AC
Souza, KR
Camorim, VLDL
Cardoso, MB
PHYSICAL CHEMISTRY CHEMICAL PHYSICS, 2003, 5 (09) : 1932 - 1940

← 1 2 3 4 5 →