BEHAVIOR OF UNDER-FILM CORROSION ON ZN AND ZN-FE ALLOY COATING IN SALT SPRAY ENVIRONMENT

被引：0
|
作者：
HAYASHI, K
ITO, Y
MIYOSHI, Y
机构：
来源：
TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN | 1991年 / 77卷 / 10期
关键词：
UNDER-FILM CORROSION; DURABILITY OF COATING AGAINST CHLORINE PENETRATION; COATING-PRECEDENCE CORROSION MECHANISM; CHARGE TRANSFER CONTROLLED CORROSION MECHANISM; MICRO CIRCUIT BETWEEN COATING AND IRON SUBSTRATE;
D O I：
10.2355/tetsutohagane1955.77.10_1688
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
The observation and analysis have been carried out at under-film corrosion tip of Zn and Zn-Fe alloy coated steel sheets after salt spray test. It has been attempted to investigate the coating corrosion mechanism with electrochemical method and to elucidate the correlation between the durability of coating against chlorine penetration and the composition of Zn-Fe alloy coating. As a result, following five conclusions have been obtained. (1) Corrosion of coated steel sheets proceeds by coating-precedence corrosion mechanism. (2) Initial corrosion product of coating is chloride of zinc. (3) Durability of coating against chlorine penetration is mainly due to coating itself corrosion resistance. (4) Coating corrosion under paint proceeds by charge transfer controlled corrosion mechanism. (5) Coating corrosion is mainly due to contribution of corrosion current by way of micro circuit between coating and iron substrate.
引用
收藏
页码：1688 / 1694
页数：7
相关论文
共 50 条
  • [11] Electroplated super-hydrophobic Zn-Fe coating for corrosion protection on magnesium alloy
    Meng, Xue
    Wang, Jin-lei
    Zhang, Jie
    Niu, Bao-long
    Gao, Xiang-hua
    Yan, Hong
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2022, 32 (10) : 3250 - 3258
  • [12] Corrosion resistance of Ni/Zn-Fe/Zn and Ni/Zn/Zn-Fe compositionally modulated multilayer coatings
    Rahsepar, M.
    Bahrololoom, M. E.
    CORROSION ENGINEERING SCIENCE AND TECHNOLOGY, 2011, 46 (01) : 70 - 75
  • [13] CORROSION PROCESS OF ZN-CO, ZN-FE AND ZN-NI ALLOY ELECTROPLATINGS
    HAGI, H
    INOKUCHI, K
    HAYASHI, Y
    HIGASHI, K
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1987, 73 (14): : 1730 - 1737
  • [14] ELECTROCHEMICAL AND CHEMICAL DISSOLUTION BEHAVIOR OF ZN-FE ALLOY COATINGS AND ITS APPLICATION TO THE ANALYSIS OF ZN-FE ALLOY LAYER
    TANIMOTO, S
    FUNAHASHI, Y
    MATSUMURA, Y
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1991, 77 (11): : 1908 - 1915
  • [15] CORROSION BEHAVIOR OF ZN-FE MECHANICALLY PLATED STEEL
    SAKODA, A
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1987, 73 (05): : S444 - S444
  • [16] Structural Properties of Zn-Fe Alloy Coatings and Their Corrosion Resistance
    Bhat, Ramesh Sooryanarayana
    Balakrishna, Manjunatha Krishna
    Parthasarathy, Poornesh
    Hegde, Ampar Chitharanjan
    COATINGS, 2023, 13 (04)
  • [17] The effects of pulse plating variables on morphology and corrosion behavior of Zn-Fe alloy coatings
    Roshanghias, A.
    Sohi, M. Heydarzadeh
    JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, 2012, 9 (02) : 215 - 218
  • [18] Under-film corrosion in an alkali environment
    Tsukada, T
    Scantlebury, JD
    ADVANCES IN CORROSION PROTECTION BY ORGANIC COATINGS III, 1998, 97 (41): : 141 - 149
  • [19] IMPROVING PAINTABILITY WITH FE-P COATING OF ZN-FE AND ZN-NI ALLOY ELECTROPLATED STEELS
    HONJO, T
    YAMATO, K
    KATO, C
    ICHIDA, T
    INTERNATIONAL JOURNAL OF VEHICLE DESIGN, 1985, 6 (4-5) : 496 - 500
  • [20] Effect of pulse plating on the composition and corrosion properties of Zn-Co and Zn-Fe alloy coatings
    Ramanauskas, Rimantas
    Gudaviciute, Laima
    Juskenas, Remigijus
    CHEMIJA, 2008, 19 (01): : 7 - 13
12345