BEHAVIOR OF UNDER-FILM CORROSION ON ZN AND ZN-FE ALLOY COATING IN SALT SPRAY ENVIRONMENT

被引：0
|
作者：
HAYASHI, K
ITO, Y
MIYOSHI, Y
机构：
来源：
TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN | 1991年 / 77卷 / 10期
关键词：
UNDER-FILM CORROSION; DURABILITY OF COATING AGAINST CHLORINE PENETRATION; COATING-PRECEDENCE CORROSION MECHANISM; CHARGE TRANSFER CONTROLLED CORROSION MECHANISM; MICRO CIRCUIT BETWEEN COATING AND IRON SUBSTRATE;
D O I：
10.2355/tetsutohagane1955.77.10_1688
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
The observation and analysis have been carried out at under-film corrosion tip of Zn and Zn-Fe alloy coated steel sheets after salt spray test. It has been attempted to investigate the coating corrosion mechanism with electrochemical method and to elucidate the correlation between the durability of coating against chlorine penetration and the composition of Zn-Fe alloy coating. As a result, following five conclusions have been obtained. (1) Corrosion of coated steel sheets proceeds by coating-precedence corrosion mechanism. (2) Initial corrosion product of coating is chloride of zinc. (3) Durability of coating against chlorine penetration is mainly due to coating itself corrosion resistance. (4) Coating corrosion under paint proceeds by charge transfer controlled corrosion mechanism. (5) Coating corrosion is mainly due to contribution of corrosion current by way of micro circuit between coating and iron substrate.
引用
收藏
页码：1688 / 1694
页数：7
相关论文
共 50 条
  • [1] EFFECT OF COATING WEIGHT AND CORROSIVE ENVIRONMENT ON UNDER-FILM CORROSION OF ZN AND ZN-FE ALLOY COATED STEEL SHEETS
    HAYASHI, K
    ITO, Y
    MIYOSHI, Y
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1992, 78 (01): : 127 - 133
  • [2] ELECTROCHEMICAL STUDY ON UNDER-FILM CORROSION MECHANISM OF ZN AND ZN-FE ALLOY COATINGS
    HAYASHI, K
    ITO, Y
    KATO, C
    MIYOSHI, Y
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1991, 77 (07): : 1122 - 1129
  • [3] BEHAVIOR AT UNDER-FILM CORROSION TIPS OF ZN-FE ALLOY COATED STEEL SHEETS
    HAYASHI, K
    ITO, Y
    KATO, C
    MIYOSHI, Y
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1990, 76 (09): : 1496 - 1503
  • [4] THEORETICAL INVESTIGATION OF UNDER-FILM CORROSION ON ZN, ZN-FE ALLOY COATED STEEL SHEETS
    HAYASHI, K
    ITO, Y
    MIYOSHI, Y
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1991, 77 (10): : 1695 - 1701
  • [5] Corrosion behavior of Zn and Zn-Fe alloy electroplated steel sheets under paint film
    NKK Corp, Kawasaki, Japan
    Zairyo to Kankyo/ Corrosion Engineering, 1996, 45 (08): : 480 - 486
  • [6] INVESTIGATION OF ZN-FE ALLOY COATING
    GHAFARI, M
    SAITO, M
    HIROSE, Y
    NAKAMURA, Y
    NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS, 1993, 76 (1-4): : 306 - 307
  • [7] Effect of Deposition Time on Thickness and Corrosion Behavior of Zn-Fe Coating
    Liu L.
    Yu S.
    Journal of Shanghai Jiaotong University (Science), 2019, 24 (03): : 395 - 401
  • [8] Effect of Deposition Time on Thickness and Corrosion Behavior of Zn-Fe Coating
    刘丽
    于思荣
    JournalofShanghaiJiaotongUniversity(Science), 2019, 24 (03) : 395 - 401
  • [9] Corrosion behavior of Zn and Zn-Fe alloy electroplated steel sheets in atmospheric exposure test
    Sagiyama, Masaru
    Hiraya, Akira
    Zairyo to Kankyo/ Corrosion Engineering, 1996, 45 (07): : 432 - 438
  • [10] Study on the behavior of Zn-Fe alloy electroplating
    Zhang, Z
    Leng, WH
    Shao, HB
    Zhang, JQ
    Wang, JM
    Cao, CN
    JOURNAL OF ELECTROANALYTICAL CHEMISTRY, 2001, 516 (1-2) : 127 - 130
12345